Fluid resistant, high performance reactive hot melt sealant and/or adhesive compositions
View Patent ↗A reactive hot melt (RHM) composition is provided as a mixture of a urethane prepolymer which is a reaction product of at least one crystallizable polyol, a perfluoropolyether polyol, and at least one isocyanate, a filler material, and a teachable plasticizer consisting of an aliphatic ester of a carboxylic acid.
1. A reactive hot melt (RHM) composition comprising a mixture of:
a urethane prepolymer which is a reaction product of (i) at least one crystallizable polyol, (ii) a perfluropolyether polyol, and (iii) at least one isocyanate;
a filler material; and
a leachable plasticizer consisting of an aliphatic ester of a carboxylic acid, wherein
the at least one isocyanate comprises a mixture of hexamethylene diisocyanate (HDI) trimer and methylenediphenyl diisocyanate (MDI) in about a 1:1 weight ratio.
2. The RHM composition as in claim 1 , wherein the at least one crystallizable polyol is selected from the group consisting of polyester polyols, polyethylene copolymer polyols, polysiloxane polyols and acrylic polyols.
3. The RHM composition as in claim 1 , further comprising at least one polyol selected from the group consisting of polyalkylene glycols, polysulfide polyols and silicone polyols.
4. The RHM composition as in claim 1 , wherein the filler material is at least one fibrous or particulate filler selected from the group consisting of silica, carbon or metallic filler materials.
5. The RHM composition as in claim 4 , wherein the filler material is at least one selected from the group consisting of nickel, iron, aluminum, tungsten, silver, gold, platinum, palladium and carbon materials.
6. The RHM composition as in claim 5 , wherein the at least one filler material is present in an amount between about 0.1 wt. % to about 80 wt. %, based on total composition weight.
7. The RHM composition as in claim 1 , wherein the leachable plasticizer consists of an aliphatic ester of citric acid, malonic acid and/or phthalic acid.
8. The RHM composition as in claim 7 , wherein the leachable plasticizer is at least one selected from the group consisting of triethyl citrate, tributyl acetylcitrate and diethyl malonate.
9. The RHM composition as in claim 8 , further comprising a non-ionic miscibilizer selected from the group consisting of ethylenediamine tetrakis(propoxylate-block-ethoxylate) tetrol (EDTP-b-ET) and poly(ethylene glycol) sorbitol hexaoleate (PEGSH).
10. The RHM composition as in claim 8 , wherein the leachable plasticizer is present in an amount between about 1.0 wt. % to about 40 wt. %, based on total composition weight.
11. The RHM composition as in claim 1 , further comprising between about 0.1 wt. % to about 80 wt. %, based on total composition weight, of at least one additive other than the filler material which is selected from the group consisting of density modifiers, dispersion additives, blocking agents, air reducing additives, antioxidants, flow improvers, conductivity modifiers and cure rate accelerators.
12. A substrate which is at least partially coated with the RHM composition of claim 1 .
13. A method of forming a coating comprising applying the RHM composition of claim 1 onto a substrate at a melt temperature of the RHM, and allowing the RHM to cure on the substrate.
14. A method of making the reactive hot melt (RHM) composition according to claim 1 , wherein the method comprises:
(a) forming the urethane prepolymer by reacting (i) the at least one crystallizable polyol, (ii) the perfluoropolyether polyol, and (iii) the at least one isocyanate; and thereafter
(b) mixing the urethane prepolymer with (1) the filler material and (2) the leachable plasticizer consisting of the aliphatic ester of a carboxylic acid.
15. A reactive hot melt (RHM) composition comprising a mixture of:
(i) a urethane prepolymer which is a reaction product of (i) at least one crystallizable polyol, (ii) a perfluropolyether polyol, and (iii) at least one isocyanate;
(ii) between about 0.1 wt. % to about 80 wt. %, based on total composition weight, of at least one filler material selected from the group consisting of nickel, iron, aluminum, tungsten, silver, gold, platinum, palladium and carbon materials;
(iii) between about 1.0 wt. % to about 40 wt. %, based on total composition weight, of at least one leachable plasticizer selected from the group consisting of triethyl citrate, tributyl acetylcitrate and diethyl malonate; and
(iv) a non-ionic miscibilizer selected from the group consisting of ethylenediamine tetrakis(propoxylate-block-ethoxylate) tetrol (EDTP-b-ET) and poly(ethylene glycol) sorbitol hexaoleate (PEGSH).
16. The RHM composition as in claim 15 , wherein the at least one isocyanate comprises a mixture of hexamethylene diisocyanate (HDI) trimer and methylenediphenyl diisocyanate (MDI) in about a 1:1 weight ratio.
17. The RHM composition as in claim 15 , wherein the at least one isocyanate is selected from the group consisting of hexamethylene diisocyanate (HDI), methylenediphenyl diisocyanate (MDI), tolulene diisocyanate (TDI), isophorone diisocyanate (IPDI) and hydrogenated methylenediphenyl diisocyanate (hMDI).
18. The RHM composition as in claim 15 , further comprising between about 0.1 wt. % to about 80 wt. %, based on total composition weight, of at least one additive other than the filler material which is selected from the group consisting of density modifiers, dispersion additives, blocking agents, air reducing additives, antioxidants, flow improvers, conductivity modifiers and cure rate accelerators.
19. A substrate which is at least partially coated with the RHM composition of claim 15 .
20. A method of forming a coating comprising applying the RHM composition of claim 15 onto a substrate at a melt temperature of the RHM, and allowing the RHM to cure on the substrate.