Compressed bone composition and methods of use thereof
The present disclosure relates to compressed bone compositions, bone implants, and variants thereof. The present disclosure also relates to methods of preparing compressed bone compositions, bone implants, and variants thereof. The present disclosure also relates to methods of using the bone compositions, bone implants and variants thereof.
1. A method for preparing a compressed bone composition, comprising:
loading bone particles into a mold with a predetermined shape,
applying pressure between about 100 psi and 1000 psi to the loaded bone particles, and freeze drying the bone particles to provide the compressed bone composition,
wherein the compressed bone composition does not comprise a binder or a chemical cross-linker.
2. The method according to claim 1 , wherein the pressure is between about 200 psi and 1000 psi.
3. The method according to claim 1 , wherein the pressure is between about 200 psi and 950 psi.
4. The method according to claim 1 , wherein said predetermined shape of the compressed bone composition comprises grooves, domes, bubbles, and/or bubble-wrap shapes.
5. The method according to claim 4 , wherein the compressed bone composition comprises holes.
6. The method according to claim 1 , wherein the compressed bone composition retains its integrity in liquid for at least 5-30 minutes.
7. The method according to claim 1 , wherein the pressure is applied at room temperature.
8. The method according to claim 1 , wherein said bone particles comprise bone fiber, bone powder, or a mixture of bone fiber and bone powder.
9. The method according to claim 1 , wherein said bone particles are from cortical bone, cancellous bone, cortical cancellous bone, or a mixture of cortical and cancellous bone.
10. The method according to claim 1 , further comprising demineralizing the bone particles prior to applying the pressure.
11. The method according to claim 1 , further comprising cleaning the bone particles prior to applying the pressure.
12. The method according to claim 11 , wherein said cleaning comprising incubating the bone particles with an antibiotic, a detergent, an alcohol, and/or a H 2 O 2 .
13. The method according to claim 11 , wherein said cleaning comprises using an antibiotic, a detergent, and alcohol.
14. The method according to claim 1 , further comprising sterilizing the compressed bone composition.
15. The method according to claim 14 , wherein the bone particles are sterilized by gamma or e-beam irradiation, ethylene oxide, or critical CO 2 .
16. The method according to claim 1 , further comprising treating the compressed bone composition with a plasticizer composition.
17. The method according to claim 16 , wherein said plasticizer composition comprises one or more plasticizers selected from the group consisting of glycerol, adonitol, sorbitol, ribitol, galactitol, D-galactose, 1,3-dihydroxypropanol, ethylene glycol, triethylene glycol, propylene glycol, glucose, sucrose, mannitol, xylitol, meso-erythritol, adipic acid, proline, hydroxyproline, polyol, and a fatty acid.
18. The method according to claim 1 , wherein said bone particles are obtained from a human, a cow, a pig, a dog, a horse, a goat, or a sheep.
19. A compressed bone composition prepared by the method according to claim 1 , wherein the compressed bone composition comprises grooves, domes, bubbles, and/or bubble-wrap shapes, and wherein the compressed bone composition does not comprise a binder or a chemical cross-linker.
20. The bone implant according to claim 19 , wherein said bone particle is from a human, a cow, a pig, a dog, a horse, a goat, or a sheep.
21. The compressed bone composition according to claim 19 , wherein said bone particles comprise bone fiber, bone powder, or a mixture of bone fiber and bone powder.
22. The compressed bone composition according to claim 19 , wherein said bone particles are demineralized.
23. The compressed bone composition according to claim 19 , wherein said bone particles have an average residual calcium content of 0.01-8 wt %.
24. The compressed bone composition according to claim 19 , wherein said bone particles have an average residual calcium content of 0.01-4 wt %.
25. The compressed bone composition according to claim 19 , wherein said bone particles are from cortical bone, cancellous bone, cortical cancellous bone, or a mixture of cortical and cancellous bone.
26. The compressed bone composition according to claim 19 , wherein said compressed bone composition further comprises at least one cell and/or at least one bioactive factor.
27. The compressed bone composition according to claim 19 , wherein said compressed bone composition has a higher density at the groove, dome, bubble, and/or bubble-wrap shape areas compared to rest of the compressed bone composition.
28. The compressed bone composition according to claim 19 , wherein the density of the compressed bone composition is between about 0.24 and 0.35 g/cm 3 .
29. The compressed bone composition according to claim 19 , wherein said bone particles have a median diameter of about 10-1,000 microns, a median length of about 0.5-100 mm, and a median thickness of about 10-1000 microns.
30. The compressed bone composition according to claim 19 , wherein the compressed bone composition comprises holes.
31. The method according to claim 1 , wherein the compressed bone composition comprises holes.