Aqueous coating composition and process of making the same
View Patent ↗An aqueous coating composition capable of providing coating films with balanced properties of high hardness, high clarity, good water resistance, and good alcohol resistance; and a process of making such aqueous coating composition.
1. An aqueous coating composition, comprising,
(a) an aqueous emulsion polymer present in an amount of from 50 to 88% by weight based on total solids weight of the coating composition;
(b) colloidal silica present in an amount of from 14 to 80%, by solids weight, based on the weight of the emulsion polymer;
(c) an alkyl silane of Formula (I):
wherein R 1 is a saturated alkyl group with more than 4 carbon atoms; R 2 is an alkoxy group with 1 to 3 carbon atoms, and n is an integer from 1 to 3; wherein the weight ratio of the alkyl silane to solids weight of the colloidal silica is from 0.11 to 0.23; and (d) water; wherein the content of volatile organic components in the coating composition is less than 150 g/L.
2. The aqueous coating composition of claim 1 , wherein R 1 is a saturated alkyl group with 8 to 16 carbon atoms.
3. The aqueous coating composition of claim 1 , wherein the alkyl silane is selected from the group consisting of octyl triethoxylsilane, octyl trimethoxylsilane, hexadecyl trimethoxy silane, hexadecyl triethoxyl silane, and mixtures thereof.
4. The aqueous coating composition of claim 1 , wherein the weight ratio of the alkyl silane to solids weight of the colloidal silica is from 0.125 to 0.2.
5. The aqueous coating composition of claim 1 , wherein the colloidal silica is present in an amount of from 17 to 66%, by solids weight, based on the weight of the emulsion polymer.
6. The aqueous coating composition of claim 1 , wherein the colloidal silica has an average particle size of no more than 100 nm.
7. The aqueous coating composition of claim 1 , wherein the emulsion polymer has a glass transition temperature of from 0 to 45° C.
8. The aqueous coating composition of claim 1 , wherein the emulsion polymer is an acrylic emulsion copolymer.
9. The aqueous coating composition of claim 8 , wherein the acrylic emulsion copolymer comprises, as copolymerized units, at least one ethylenically unsaturated monomer having a functional group selected from the group consisting of carbonyl, acetoacetate, alkoxysilane, carboxyl, ureido, amide, imide, amino group, and mixtures thereof.
10. The aqueous coating composition of claim 1 , further comprising one or more selected from the group consisting of a coalescent, a solvent, a wetting agent, a defoamer, a thickener, a rheology modifier, a matting agent, a dispersant, a wax dispersion, and mixtures thereof.
11. The aqueous coating composition of claim 1 , having a pigment volume concentration of from 0 to 20%.
12. An aqueous coating composition comprising,
(a) from 60 to 86.4% by weight, based on total solids weight of the coating composition, an acrylic emulsion copolymer comprising, as copolymerized units, at least one ethylenically unsaturated nonionic monomer and at least one ethylenically unsaturated monomer having a functional group selected from the group consisting of carbonyl, acetoacetate, alkoxysilane, carboxyl, ureido, amide, imide, amino group, and mixtures thereof;
(b) from 17 to 42% by solids weight of colloidal silica, based on the weight of the emulsion polymer;
(c) an alkyl silane of Formula (I):
wherein R 1 is a saturated alkyl group with 6 to 16 carbon atoms; R 2 is an alkoxy group with 1 to 3 carbon atoms, and n is an integer from 1 to 3; wherein the weight ratio of the alkyl silane to solids weight of the colloidal silica is from 0.15 to 0.2;
(d) water;
(e) from 0.5 to 4.5% by weight of a coalescent, based on total solids weight of the coating composition;
(f) from 0 to 4% by weight of a matting agent, based on total solids weight of the coating composition; and
(g) from 0 to 1% by weight of a crosslinking agent, based on total solids weight of the coating composition;
wherein the content of volatile organic components in the coating composition is less than 150 g/L.
13. A process of preparing the aqueous coating composition of of claim 1 , comprising: admixing
(a) an aqueous emulsion polymer present in an amount of from 50 to 88% by weight based on total solids weight of the coating composition;
(b) colloidal silica present in an amount of from 14 to 80%, by solids weight, based on the weight of the emulsion polymer;
(c) an alkyl silane of Formula (I):
wherein R 1 is a saturated alkyl group with more than 4 carbon atoms; R 2 is an alkoxy group with 1 to 3 carbon atoms, and n is an integer from 1 to 3; wherein the weight ratio of the alkyl silane to solids weight of the colloidal silica is from 0.11 to 0.23; and
(d) water;
wherein the content of volatile organic components in the coating composition is less than 150 g/L.
14. The aqueous coating composition of claim 1 , wherein the colloidal silica is non-neutral.