Electrodeposited copper foil, and electrical component and battery comprising same
Disclosed is an electrodeposited copper foil, in which a center line roughness average Ra (μm), a maximum height Rmax (μm), and a ten-point height average Rz (μm) of a matte side satisfy an Equation below, 1.5≤(Rmax−Rz)/Ra≤6.5. The electrodeposited copper foil according to the present invention maintains low roughness and high strength, and exhibits a high elongation rate, and particularly, has excellent glossiness, so that the electrodeposited copper foil may be used in a current collector of a medium and large lithigum ion secondary battery and a semiconductor packaging substrate for Tape Automated Bonding (TAB) used in a Tape Carrier Package (TCP).
1. An electrodeposited copper foil for a current collector of a battery, in which a center line roughness average Ra (μm), a maximum height Rmax (μm), and a ten-point height average Rz (μm) of a matte side for adjusting a height deviation and shapes of surface elements of the matte side satisfy an Equation below,
4.27≤( R max− Rz )/ Ra ≤6.5,
wherein Rz satisfies an equation: Rz≤1.4 μm, and wherein a tensile strength of the electrodeposited copper foil before a heat treatment is 40 kgf/mm 2 to 50 kgf/mm 2 a room temperature.
2. The electrodeposited copper foil of claim 1 , wherein an elongation rate of the electrodeposited copper foil is 6% to 15% at a room temperature.
3. The electrodeposited copper foil of claim 1 , wherein a tensile strength and an elongation rate of the electrodeposited copper foil after a heat treatment for one hour at 180° C. is 40 kgf/mm 2 to 50 kgf/mm 2 and 7% to 15%, respectively.
4. The electrodeposited copper foil of claim 3 , wherein the tensile strength of the electrodeposited copper foil after the heat treatment is 85% to 99% of a tensile strength of the electrodeposited copper foil before the heat treatment.
5. The electrodeposited copper foil of claim 3 , wherein the elongation rate after the heat treatment is one time to 4.5 times of an elongation rate of the electrodeposited copper foil before the heat treatment.
6. The electrodeposited copper foil of claim 1 , wherein a corner curl angle of the electrodeposited copper foil is 0° to 45°.
7. The electrodeposited copper foil of claim 1 , wherein a corner curl height of the electrodeposited copper foil is 0 mm to 40 mm.
8. The electrodeposited copper foil of claim 1 , wherein the electrodeposited copper foil has a thickness of 2 μm to 10 μm.