Method for synthesizing silicoaluminophosphate-34 molecular sieves
View Patent ↗A method for synthesizing small crystals of silicoaluminophosphate-34 (SAPO-34) molecular sieves with high structural purity. The method includes forming a first slurry and a second slurry which are aged separately to form a first aged slurry and a second aged slurry. The first slurry includes a first source of phosphorus, a first source of aluminium, a first source of silicon, and at least one first organic structure directing agent. The second slurry includes a second source of phosphorus, a second source of aluminium, a second source of silicon, and at least one second organic structure directing agent. Then, the first aged slurry and the second aged slurry are combined to form a mixture of aged slurries. Finally, crystallization of silicoaluminophosphate molecular sieves comprising the SAPO-34 molecular sieves is induced from the mixture of aged slurries.
1. A method for synthesizing silicoaluminophosphate-34 (SAPO-34) molecular sieves, comprising:
forming a first slurry comprising a first source of phosphorus, a first source of aluminium, a first source of silicon, and at least one first organic structure directing agent;
aging the first slurry to form a first aged slurry;
forming a second slurry comprising a second source of phosphorus, a second source of aluminium, a second source of silicon, and at least one second organic structure directing agent;
aging the second slurry to form a second aged slurry;
forming a mixture of aged slurries by combining the first aged slurry and the second aged slurry; and
inducing crystallization of silicoaluminophosphate molecular sieves comprising the SAPO-34 molecular sieves from the mixture of aged slurries;
wherein at least one first organic structure directing agent in the first slurry is different from at least one second organic structure directing agent in the second slurry;
the first source of phosphorus may be the same or different from the second source of phosphorus;
the first source of aluminium may be the same or different from the second source of aluminium; and
the first source of silicon may be the same or different from the second source of silicon.
2. The method of claim 1 , wherein forming the first slurry comprises:
combining the first source of phosphorus and water to form a first phosphoric solution;
introducing the first source of aluminium into the first phosphoric solution;
introducing the first source of silicon into the first phosphoric solution after the introduction of the first source of aluminium; and
introducing at least one first organic structure directing agent into the first phosphoric solution after the introduction of the first source of silicon.
3. The method of claim 1 , wherein forming the second slurry comprises:
combining the second source of phosphorus and water to form a second phosphoric solution;
introducing at least one second organic structure directing agent into the second phosphoric solution;
introducing the second source of aluminium into the second phosphoric solution after the introduction of at least one second organic structure directing agent; and
introducing the second source of silicon into the second phosphoric solution after the introduction of the second source of aluminium.
4. The method of claim 1 , wherein the first slurry is aged to produce crystal nuclei precursors, nuclei and/or crystallites for SAPO-34 in the first aged slurry.
5. The method of claim 1 , wherein aging the first slurry is performed by aging the first slurry at a temperature within the range from about room temperature to about 200° C. for any period of time longer than 0.5 hours.
6. The method of claim 1 , wherein aging the first slurry is performed by aging the first slurry at a temperature within the range from about 20° C. to about 150° C. for a time within the range from about 1 hour to about 30 hours.
7. The method of claim 1 , wherein the second slurry is aged to produce SAPO building units with no or a very small amount of crystal nuclei precursors, nuclei, and crystallites for SAPO structures other than SAPO-34 in the second aged slurry.
8. The method of claim 1 , wherein aging the second slurry is performed by aging the second slurry at a temperature within the range from about 10° C. to about 150° C. for a time within the range from about 0.5 hour to about 50 hours.
9. The method of claim 1 , wherein aging the second slurry is performed by aging the second slurry at a temperature within the range from about 20° C. to about 100° C. for a time within the range from about 1 hour to about 30 hours.
10. The method of claim 1 , wherein at least one first organic structure directing agent is a nitrogen compound.
11. The method of claim 1 , wherein at least one second organic structure directing agent is a nitrogen compound.
12. The method of claim 1 , wherein at least one first organic structure directing agent is selected from the group consisting of quaternary ammonium compounds, alkanolamines, and substituted or unsubstituted alkylamines.
13. The method of claim 1 , wherein at least one first organic structure directing agent is tetraethylammonium hydroxide.
14. The method of claim 1 , wherein at least one second organic structure directing agent is selected from the group consisting of quaternary ammonium compounds, alkanolamines, and substituted or unsubstituted alkylamines.
15. The method of claim 1 , wherein at least one second organic structure directing agent is selected from the group consisting of alkanolamines and alkylamines.
16. The method of claim 1 , wherein the weight percentage of the first aged slurry in the mixture of aged slurries is within the range from about 1% to about 99%.
17. The method of claim 1 , wherein the weight percentage of the first aged slurry in the mixture of aged slurries is within the range from about 10% to about 80%.
18. The method of claim 1 , wherein the weight percentage of the first aged slurry in the mixture of aged slurries is within the range from about 20% to about 50%.
19. The method of claim 1 , wherein the inducing crystallization step comprises:
initially heating the mixture of aged slurries to a first temperature within the range from about 50° C. to about 200° C. and then holding the mixture at the first temperature for a time within the range from about 0.5 hour to about 24 hours; and
further heating the mixture of aged slurries to a second temperature within the range from about 150° C. to about 250° C. and then holding the mixture at the second temperature for a time within the range from about 0.5 hour to about 70 hours.
20. The method of claim 1 , wherein the inducing crystallization step comprises:
initially heating the mixture of aged slurries to a first temperature within the range from about 80° C. to about 150° C. and then holding the mixture at the first temperature for a time within the range from about 1 hour to about 10 hours; and
further heating the mixture of aged slurries to a second temperature within the range from about 150° C. to about 220° C. and then holding the mixture at the second temperature for a time within the range from about 1 hour to about 50 hours.
21. The method of claim 1 , wherein the inducing crystallization step comprises:
heating the mixture of aged slurries to a temperature within the range from about 150° C. to about 250° C. and then holding the mixture at the temperature for a time within the range from about 0.5 hour to about 70 hours.
22. The method of claim 1 , wherein the inducing crystallization step comprises:
heating the mixture of aged slurries to a temperature within the range from about 150° C. to about 220° C. and then holding the mixture at the temperature for a time within the range from about 1 hour to about 50 hours.
23. The method of claim 1 , wherein the silicoaluminophosphate molecular sieves comprise at least 90% of the SAPO-34 molecular sieves.
24. The method of claim 1 , wherein the silicoaluminophosphate molecular sieves comprise at least 95% of the SAPO-34 molecular sieves.
25. The method of claim 1 , wherein the average diameter of the SAPO-34 molecular sieves is smaller than 3 μm.
26. The method of claim 23 , wherein the average diameter of the SAPO-34 molecular sieves is smaller than 3 μm.
27. A catalyst particle for the conversion of methanol to olefins comprising the SAPO-34 molecular sieves of claim 1 .
28. A catalyst particle for the conversion of methanol to olefins comprising the SAPO-34 molecular sieves of claim 26 .
29. A process for producing olefins, the process comprising converting methanol to olefins in the presence of the catalyst particle of claim 28 .