Spot welded joint and spot welding method
The present invention has as its object to provide a spot welded joint and spot welding method which raise the fracture toughness of spot welded metal to raise the strength of the spot welded joint. In the present invention, there is provided a spot welding method comprising a melt zone forming step forming a melt zone by conduction and, after the melt zone forming step, a solidification step of running a current lower than the current run in the melt zone forming step so as to cause the melt zone to solidify, wherein, in the solidification step, electromagnetic vibration is applied to the melt zone, and a frequency f V of the electromagnetic vibration, a solidification speed ν S when the melt zone solidifies, and an arm interval of dendrites λ D when the melt zone solidifies satisfy 0.2≤ν S /(λ D ·f V )≤4.0.
1. A spot welding method comprising:
superposing at least two steel sheets;
forming a melt zone by conduction,
wherein the conduction is performed by running a current having a value,
after said melt zone forming, forming a solidified structure in the melt zone running another current of which value is lower than the value for forming the melt zone, and applying an electromagnetic vibration, and
wherein a frequency f V of the electromagnetic vibration, a solidification speed ν S when the melt zone solidifies, and an arm interval of dendrites λ D when the melt zone solidifies satisfy 0.2≤ν S /(λ D ·f V )≤4.0, and
the solidification speed ν S and the arm interval of the dendrites λ D are obtained by advance experiments, wherein:
the solidification speed ν S and the arm intervals of the dendrites λ D are obtained by applying spot welding to samples of which combination of sheet and type of steel are the same as in the steel sheets to be welded while putting time of running current under plural conditions.