The present invention provides polyamide compositions comprising (a) at least one high chain-length polyamide [polyamide (PA)]; (b) at least one grafted polyolefin [olefin (PO)]; and (c) at least one aromatic diacid [acid (DA)]. The polyamide composition can be advantageously used as a material to be coated on a surface of metal component.
1. An article, comprising a metal component having a surface coated with a polyamide composition, wherein the polyamide composition comprises:
(a) at least one high chain-length polyamide in an amount ranging from 68 to 94.5% by weight, relative to the total weight of the polyamide composition;
(b) at least one grafted polyolefin in an amount ranging from 5 to 30% by weight, relative to the total weight of the polyamide composition; and
(c) at least one aromatic diacid in an amount ranging from 0.5 to 5.0% by weight, relative to the total weight of the polyamide composition,
wherein the high chain-length polyamide is polyamide 6,10,
wherein the aromatic diacid is selected from the group consisting of isophthalic acid and terephthalic acid, and
wherein the at least one grafted polyolefin comprises a high- or low-density polyethylene grafted with maleic anhydride.
2. The article according to claim 1 , wherein the polyamide composition further comprises one or more additive selected from the group consisting of antioxidant, heat stabilizer, UV stabilizer, colorant, lubricant, plasticizer, and any combination thereof.
3. The article according to claim 1 , wherein the metal component comprises aluminum.
4. The article according to claim 1 , wherein the article is suitable for use in an air-conditioner, a refrigerator, a dishwasher, or a metallic spring application.
5. The article according to claim 1 , wherein the aromatic diacid is isophthalic acid.
6. The article according to claim 1 , wherein the amount of the aromatic diacid is from 0.5 to 2.0% by weight, relative to the total weight of the polyamide composition.
7. A method for improving adhesion of a thermoplastic polyamide polymer composition to metal, comprising adding at least one grafted polyolefin in an amount ranging from 5 to 30% by weight, relative to the total weight of the thermoplastic polyamide composition wherein the at least one grafted polyolefin comprises a high- or low-density polyethylene grafted with maleic anhydride, and at least one aromatic diacid in an amount ranging from 0.5 to 5.0% by weight, relative to the total weight of the thermoplastic polyamide composition, wherein the aromatic diacid is selected from the group consisting of isophthalic acid and terephthalic acid, as an adhesion promoter in the thermoplastic polyamide polymer composition and applying the thermoplastic polyamide polymer composition to metal, wherein the thermoplastic polyamide polymer composition further comprises at least one high chain-length polyamide, wherein the high chain-length polyamide is polyamide 6,10, and wherein the high chain-length polyamide is present in an amount ranging from 68 to 94.5% by weight, relative to the total weight of the polyamide composition.