Lithium-nickel based positive electrode active material, method of preparing the same, and lithium secondary battery including the same
View Patent ↗The present disclosure relates to a positive electrode active material which reduces lithium by-products and improves structural stability and includes a lithium-nickel based transition metal composite oxide in which an alkaline earth metal having oxidation number of +2 is doped and a phosphate coated layer formed on the outer surface of the composite oxide. Accordingly, a second battery including the positive electrode active material has excellent capacity characteristics, and also improves structural stability during charging/discharging and prevents swelling, thereby being capable of exhibiting excellent life characteristics. Therefore, the present invention may be easily applied to industry in need thereof, and particularly to electric vehicles industry requiring high capacity and long-term life characteristics.
1. A lithium secondary battery comprising:
a positive electrode in which a current collector is coated with a slurry comprising a positive electrode active material,
wherein the positive electrode active material comprises:
a lithium-nickel based transition metal composite oxide having a layered structure, which is expressed by Chemical Formula 1 below; and
a phosphate coating layer formed on the surface of the composite oxide,
Li x Ni a M b A w O 2-y D y [Chemical Formula 1]
where, 1.0≤x≤1.2, 0.5≤a≤1, 0<b≤0.3, 0≤y<0.2, 0<w≤0.3, and 2≤x+a+b+w≤2.2,
M is Mn b1 Co b2 , where, 0<b1+b2≤0.3,
A is Sr, and
D is at least one selected from the group consisting of S, N, F, Cl, Br, I, and P,
wherein the content of nickel in the positive electrode active material is 70 mol % or more based on the total amount of metallic components excluding lithium,
wherein a phosphate precursor as a raw material of the phosphate is at least one selected from the group consisting of (NH 4 ) 2 HPO 4 , (NH 4 ) 2 H 2 PO 4 , (NH 4 ) 3 PO 4 .(3H 2 O), H 3 PO 4 , and P 2 O 5 and the phosphate coating layer has a thickness of 1 to 100 nm,
wherein the phosphate coating layer comprises Li 3 PO 4 ,
wherein a total amount of Li 2 CO 3 and LiOH on a surface of the positive electrode active material is 0.276 wt % or less, and
wherein the lithium secondary battery has a capacity retention ratio of 90% or more compared to the initial capacity, after 55 cycles under 1.0C charge and 1.0C discharge condition at 45° C.
2. The lithium secondary battery of claim 1 , wherein Sr is located at lithium sites or vacant sites in crystal lattices.