Laminated substrate using fiber-reinforced thermoplastic plastic, and molded product manufacturing method using same
Provided is a laminated substrate wherein a sheet-shaped material with a porosity of 50-99% is laminated onto at least one surface of a prepreg substrate which includes a reinforcing fiber and a thermoplastic resin.
1. A pre-molded laminated substrate, comprising a sheet having a porosity of from 50% to 99% laminated on at least one surface of a prepreg substrate including reinforcing fibers and a thermoplastic resin, wherein:
a length of the reinforcing fibers that constitute the prepreg substrate is of from 10 mm to 100 mm, and the prepreg substrate and the sheet are not adhered,
the sheet comprises a nonwoven fabric,
the sheet is not impregnated with the thermoplastic resin of the prepreg substrate, the pre-molded laminated substrate is obtained by being cut out, and
30% to 50% by area of a total area of at least one surface of the prepreg substrate is covered by the sheet.
2. The pre-molded laminated substrate according to claim 1 , wherein the prepreg substrate comprises a plurality of prepreg sheets laminated to each other wherein each prepreg sheet includes the reinforcing fibers unidirectionally oriented in the thermoplastic resin.
3. The pre-molded laminated substrate according to claim 1 , wherein the prepreg substrate comprises fiber bundles of the reinforcing fibers dispersed in the thermoplastic resin.
4. The pre-molded laminated substrate according to claim 1 , wherein the prepreg substrate comprises rectangular chips of a prepreg including the reinforcing fibers unidirectionally oriented, or dispersed in a random fashion in the thermoplastic resin.
5. The pre-molded laminated substrate according to claim 1 , wherein the thickness of the sheet is of from 0.01 mm to 10 mm.
6. A laminated substrate obtained by stamping molding of the pre-molded laminated substrate of claim 1 .
7. The pre-molded laminated substrate according to claim 1 , wherein the sheet is a polyester nonwoven fabric.
8. The pre-molded laminated substrate according to claim 1 , wherein the sheet is a glass nonwoven fabric.
9. The pre-molded laminated substrate according to claim 1 , wherein the sheet has the porosity of from 90 to 95% before the stamping molding.
10. The pre-molded laminated substrate according to claim 1 , wherein the nonwoven fabric is a heat insulating, layer.
11. The pre-molded laminated substrate according to claim wherein the sheet is an outermost layer of the laminated substrate.