Fuser belt to be used in an electrophotographic printer
View Patent ↗This invention discloses a polyimide fuser belt incorporating synthetic graphite or expanded synthetic graphite as a filler. The resulting fuser belt has increased thermal diffusivity without sacrificing mechanical strength. Fuser belts made with synthetic or expanded synthetic graphite enable electrophotographic printers to exhibit superior fuse temperatures and better print speeds across a range of different media types.
1. A seamless endless belt for a heat fuser having a polyimide resin body and synthetic graphite incorporated within the polyimide resin body as a filler, wherein the seamless endless belt having the synthetic graphite filler has increased thermal diffusivity without sacrificing mechanical strength, wherein the synthetic graphite is expanded graphite, wherein the polyimide is a reaction product of a polyamic acid solution of 3,3′,4,4′ biphenyltetracarboxylic dianhydride and p-phenylenediamine in a polar aprotic solvent 65° C., and wherein the synthetic graphite can range from about 5% to about 50% based on the weight of polyamic acid solids.
2. The seamless endless belt of claim 1 , wherein the expanded synthetic graphite is synthesized using an intercalation compound of graphite that expands when heated.
3. The seamless endless belt of claim 1 , wherein the polar aprotic solvent is N-methylpyrrolidinone.
4. A toner fixing system comprising
a heating element to generate heat for fusing electrophotographic toner;
a seamless endless belt with a surface in contact with said heating element movable in contact with said heating element;
a back up member in nip position with said belt where said belt contact said heating element; and
a media feed path to feed media carrying unfixed toner images through said nip;
wherein the seamless endless belt has a polyimide resin body and synthetic graphite incorporated within the polyimide resin body as a filler, wherein the polyimide is a reaction product of a polyamic acid solution of 3,3′,4,4′ biphenyltetracarboxylic dianhydride and p-phenylenediamine in a polar aprotic solvent at 65° C., and wherein the synthetic graphite can range from about 5% to about 50% based on the weight of polyamic acid solids.
5. The toner fixing system of claim 4 , wherein the synthetic graphite is expanded graphite.
6. The toner fixing system of claim 5 , wherein the expanded synthetic graphite is synthesized using an intercalation compound of graphite that expands when heated.
7. The toner fixing system of claim 4 , wherein the polar aprotic solvent is N-methylpyrrolidinone.