Multilayer brazing sheet for vacuum braze applications
View Patent ↗A five layer sheet for vacuum brazing has a core layer of 3XXX aluminum alloy and two interliner layers of 5XXX aluminum alloy bonded to the core layer. Two layers of 4XXX aluminum alloy are bonded to the two interliner layers. An elevated quantity of Mg in the interliner layers can provide enhanced strength, facilitate brazing and provide corrosion protection. A low zinc composition for the sheet also facilitates vacuum brazing.
1. A sheet material for brazing, comprising:
a core of a homogenized 3xxx aluminum alloy;
a first interliner on a first side of the core;
a second interliner on a second side of the core;
a first braze liner on the first interliner;
and a second braze liner on the second interliner, wherein the first and second interliners are formed from an aluminum alloy having, in weight %; 0.1-0.40 Si; 0.10-0.5 Fe; up to 0.05 Cu; up to 0.3 Mn; 0.3-1.10 Mg; up to 0.05 Cr; up to 0.05 Zn; 0.05-0.2 Ti, the remainder being aluminum and impurities and wherein the first and second braze liners are each formed from a 4xxx aluminum alloy.
2. The sheet material of claim 1 , wherein the first and second interliners comprise, in weight %, 0.12-0.4 Si.
3. The sheet material of claim 1 , wherein the first and second interliners comprise in weight %, up to 0.4 Fe.
4. The sheet material of claim 1 , wherein the first and second interliners comprise, in weight %, up to 0.03 Cu.
5. The sheet material of claim 1 , wherein the first and second interliners comprise, in weight %, up to 0.3 Mn.
6. The sheet material of claim 1 , wherein the first and second interliners comprise, in weight %, 0.3-1.0 Mg.
7. The sheet material of claim 1 , wherein the first and second interliners each comprise, in weight %, up to 0.03 Cr.
8. The sheet material of claim 1 , wherein the first and second interliners each comprise, in weight %, up to 0.03 Zn.
9. The sheet material of claim 1 , wherein the first and second interliners each comprise, in weight %, up to 0.3 Fe.
10. The sheet material of claim 1 , wherein the first and second interliners each comprise, in weight %, 0.08-0.16 Ti.
11. The material of claim 1 , wherein the core layer is treated by a pre-hot rolling thermal treatment.
12. The material of claim 1 , wherein the first braze liner and the second braze liner each have a max Zn level of 0.2 wt %.
13. The material of claim 1 , wherein the first braze liner and the second braze liner each have Mg in an amount from 0.16 to 2.5 wt %.
14. The material of claim 1 , wherein the core comprises in wt % 0.1 to 1.0 Si, up to 0.6 Fe, 0.3 to 0.8 Cu, 1.0 to 1.6 Mn, 0.1 to 0.6 Mg, up to 0.03 Cr, up to 0.05 Zn and 0.1-0.2 Ti, the remainder being Al and impurities.
15. The material of claim 14 , wherein the core comprises in wt % 0.05-0.1 Si, 0.1-0.2 Fe, 0.4-0.6 Cu, 1.0-1.3 Mn, 0.1-0.3 Mg, 0.002-0.006 Cr, 0.01-0.02 Zn and 0.15-0.18 Ti.
16. The material of claim 14 , wherein the core comprises in wt % 0.5 to 0.9 Si, 0.3 to 0.7 Fe, 0.4 to 0.7 Cu, 1.0 to 1.5 Mn, 0.2 to 0.5 Mg.
17. The material of claim 12 , wherein Zn is not purposely added to either of the first braze liner or the second braze liner.
18. The material of claim 1 , wherein at least one of the first interliner or the second interliner comprise in wt % 0.2-0.4 Si, 0.1-0.2 Fe, 0.01-0.04 Cu, 0.01-0.05 Mn, 0.3-0.5 Mg, 0.01-0.04 Cr and 0.01-0.04 Zn and 0.02 0.08 Ti.
19. The material of claim 1 , wherein at least one of the first interliner or the second interliner comprise in wt % 0.1-0.18 Si, 0.13-0.2 Fe, 0.001-0.01 Cu, 0.001-0.005 Mn, 0.4-0.7 Mg and 0.001-0.006 Zn.
20. The material of claim 1 , wherein at least one of the first interliner or the second interliner comprise in wt % 0.1-0.18 Si, 0.13-0.2 Fe, 0.001-0.003 Cu, 0.001-0.005 Mn, 0.5-1.05 Mg and 0.001-0.005 Zn.
21. The material of claim 1 , wherein the first braze liner in wt % 9.0 11.0 Si, up to 1.0 Fe, 0.1-0.3 Cu, up to 0.20 Mn, 0.5-2.5 Mg, up to 0.05 Zn, the remainder being Al and impurities.
22. The material of claim 1 , wherein the second braze liner in wt % 11.5-12.5 Si, 0.1-0.3 Fe, 0.1-0.3 Cu, 0.01-0.1 Mn, 0.1-0.2 Mg, 0.001-0.01 Cr, 0.01-0.05 Zn and 0.01-0.02 Ti, the remainder being Al and impurities.
23. The material of claim 21 , wherein the second braze liner comprises in wt % 11.5-12.5 Si, 0.1-0.3 Fe, 0.1-0.3 Cu, 0.01-0.1 Mn, 0.1-0.2 Mg, 0.001-0.01 Cr, 0.01-0.05 Zn and 0.01-0.02 Ti, the remainder being Al and impurities.
24. The material of claim 15 , wherein the first braze liner and the second braze liner are the first braze liner and the second braze liner of claim 23 .
25. The material of claim 16 , wherein the first braze liner and the second braze liner are the first braze liner and the second braze liner of claim 23 .
26. The material of claim 1 , wherein the clad ratio is 8-18% for each of the first braze liner and the second braze liner and 8-18% for each of the first interliner and the second interliner.