Diamond coated tool
The present invention provides a diamond coated tool which is resistant to exfoliation at an interface between a base material and a diamond layer. The diamond coated tool of the present invention is a diamond coated tool including a base material and a diamond layer coating a surface of the base material, and characterized in that the surface of the base material has an arithmetic average roughness Ra of not less than 0.1 μm and not more than 10 μm and an average length of roughness profile elements RSm of not less than 1 μm and not more than 100 μm, and that the diamond layer has a plurality of cavities extending from a portion bordering on the base material in a crystal growth direction.
1. A diamond coated tool comprising:
a base material; and
a diamond layer coating a surface of said base material,
the surface of said base material having an arithmetic average roughness Ra of not less than 0.1 μm and not more than 10 μm and an average length of roughness profile elements RSm of not less than 1 μm and not more than 100 μm, and
said diamond layer having a plurality of cavities at a portion bordering on said base material.
2. The diamond coated tool according to claim 1 , wherein
said arithmetic average roughness Ra is not less than 0.4 μm and not more than 4 μm, and
said average length of roughness profile elements RSm is not less than 2 μm and not more than 20 μm.
3. The diamond coated tool according to claim 1 , wherein
in a given section taken through said diamond coated tool at a plane including said base material and said diamond layer, the number of said cavities relative to a length of said base material is not less than 1×10 3 /cm and not more than 1×10 6 /cm.
4. The diamond coated tool according to claim 1 , wherein
said diamond layer is made of polycrystalline diamond.
5. The diamond coated tool according to claim 1 , wherein
said diamond layer is formed by chemical vapor deposition process.