Nickel-based brazing foil and process for brazing
View Patent ↗An amorphous, ductile brazing foil is provided. According to one example embodiment, the composition consists essentially of Ni rest Cr a B b P c Si d with 2 atomic percent≤a≤30 atomic percent; 0.5 atomic percent≤b≤14 atomic percent; 2 atomic percent≤c≤20 atomic percent; 0 atomic percent≤d≤14 atomic percent; incidental impurities≤0.5 atomic percent; rest Ni, where c>b>c/15 and 10 atomic percent≤b+c+d≤25 atomic percent.
1. An amorphous, ductile Ni-based brazing foil having a composition consisting essentially of
Ni rest Cr a B b P c Si d C e X f Y g
wherein a, b, c, d, e, f, and g are numbers such that 16 atomic percent≤a≤30 atomic percent; 0.5 atomic percent≤b≤14 atomic percent; 2 atomic percent≤c≤20 atomic percent; 0 atomic percent≤d≤14 atomic percent; 0 atomic percent≤e≤5 atomic percent; 0 atomic percent<f≤3 atomic percent; 0 atomic percent<g≤5 atomic percent; wherein incidental impurities are present, if at all, in amounts≤0.5 atomic percent; wherein rest indicates that the balance of the composition is Ni; wherein c>b>c/15; wherein 10 atomic percent≤b+c+d≤25 atomic percent, wherein X is one or more of the elements Mo, Nb, Ta, W and Cu; and wherein Y is one or both of the elements Fe and Co,
and wherein the foil varies in thickness from a mean thickness of the foil in a variation of less than 25% over a length of 200 m, the foil has a width B of 0.5 mm≤B≤300 mm, and the brazing foil is at least 50% amorphous.
2. The amorphous, ductile brazing foil in accordance with claim 1 , wherein the B content b is such that 1 atomic percent≤b≤8 atomic percent.
3. The amorphous, ductile brazing foil in accordance with claim 1 , wherein the P content c is such that 5 atomic percent≤c≤18 atomic percent.
4. The amorphous, ductile brazing foil in accordance with claim 1 , wherein the Si content d is such that d=0 atomic percent.
5. The amorphous, ductile brazing foil in accordance with claim 1 , wherein the Si content d is such that 0 atomic percent<d≤14 atomic percent.
6. The amorphous, ductile brazing foil in accordance with claim 1 , wherein the Y content g is 0 atomic percent≤g≤1 atomic percent.
7. The amorphous, ductile brazing foil in accordance with claim 1 , wherein the brazing foil is at least 80% amorphous.
8. The amorphous, ductile brazing foil in accordance claim 1 , wherein the foil has a thickness D of 15 μm≤D≤75 μm.
9. The amorphous, ductile brazing foil in accordance with claim 1 , wherein the width B is 30 mm≤B≤150 mm.
10. The amorphous, ductile brazing foil in accordance with claim 1 , wherein the foil varies in thickness from a mean thickness of the foil in a variation of less than 20% over a length of 100 m.
11. The amorphous, ductile brazing foil in accordance with claim 1 , wherein the foil varies in thickness from a mean thickness of the foil in a variation of less than 10% over a length of 5000 m.
12. The amorphous, ductile brazing foil in accordance with claim 1 , wherein the foil varies in thickness from a mean thickness of the foil in a variation of less than 15 μm over a length of 100 m.
13. A brazed object having a first part joined to a second part by a solder seam produced by heating the brazing foil of claim 2 .
14. The brazed object in accordance with claim 13 , wherein both the first part and the second part are made of a stainless steel.
15. The brazed object in accordance with claim 14 , wherein the solder seam has a thickness that is >15 μm.
16. The brazed object in accordance with claim 14 , wherein the brazed object is a heat exchanger.
17. The brazed object of claim 16 , wherein the heat exchanger is an exhaust gas recirculation cooler or an oil cooler.
18. The brazed object of claim 15 , wherein the brazed object is a heat exchanger.