Curable transparent rubber composition, a cured transparent rubber composition made thereof, and manufacturing process for the same

1. A solid curable, transparent, rubber composition that once cured has a haze of less than 30% and a total light transmission of more than 80%, both measured according to ASTM D1003-13, comprising:

Component (a): from 35-60 wt. % of one or more synthetic isoprene polymers having a refractive index of between 1.500 to 1.525 at 23° C.;

Component (b): from 35-60 wt. % of one or more transparent polymers different from isoprene polymers wherein the difference between the refractive indices of component (a) and (b) is 0.100 or less;

Components (c) and (d): from 0.05-8.0 wt. % of a curing agent, optionally with a co-agent, and

Component (e): from 0.01-20 wt. % of additives that do not influence the transparency,

characterized in that the composition further comprises:

Component (f): from 1-4 wt. % of one or more polyalkenamers, wherein all amounts are in percentages by weight on the total composition.

2. The composition according to claim 1 , wherein component (a) is a homopolymer of isoprene.

3. The composition according to claim 1 , wherein component (a) is a homopolymer of isoprene, made by anionic polymerization.

4. The composition according to claim 1 , wherein component (a) is present in an amount of 40-55 wt. %.

5. The composition according to claim 1 , wherein the difference between the refractive indices of component (a) and (b) is 0.050 or less.

6. The composition according to claim 5 , wherein component (b) has a mixing processing temperature of at most 150° C.

7. The composition according to claim 6 , wherein component (b) is selected from one or more of the group comprising butadiene polymer, polymers made from C 4 to C 20 olefins; thermoplastic elastomers (TPEs), styrene-butadiene rubber (SBR), ethylene-propylene rubber (EPM), ethylene-propylene-diene rubber (EPDM), urethane rubber.

8. The composition according to claim 1 , wherein component (b) is a syndiotactic 1,2-polybutadiene rubber.

9. The composition according to claim 1 , wherein component (b) is present in an amount of 40-55 wt. %.

10. The composition according to claim 1 , wherein component (c) is a peroxide.

11. The composition according to claim 10 , wherein a co-agent (d) is used in a weight ratio (c) to (d) of 1:2-10.

12. The composition according to claim 1 , wherein component (f) is a trans-polyoctenamer, preferably having a trans content of about 80%.

13. The composition according to claim 1 , having at least one of the following properties:

A Type A Durometer hardness (30 sec) of 25 or more, measured according to ASTM D2240;

A Tear Strength of 10 N/mm or more, measured according to ASTM D624, and

An abrasion resistance of 200 mm3 or less, measured according to ISO 4649, method A.

14. A process for manufacturing a transparent, cured rubber composition from the composition according to claim 1 , wherein the process comprises the steps of:

mixing components (a), (b) and (f) to obtain a mixture thereof;

adding a curing agent (c) and optionally a co-agent (d); and

uniformly kneading the mixture and curing the same.

15. An article based on the composition according to claim 1 .

16. The article according to claim 15 , wherein the article is selected from the group consisting of footwear, tires, clothes and underclothes, rain gears, eyewear, masks, toys, damping materials, building materials, coatings for wiring, packaging materials, protective members for computers, computer peripherals, contraceptive devices, sex toys, artificial nipples, paper diapers, stationery, containers, food trays, balls for sports, ball chairs, and protection films, seals, and key covers.

17. The article according to claim 16 , wherein the article is a transparent sole of a shoe.

18. An article having a composition prepared by the process according to claim 14 .