Synthesis of 2,3,3,3-tetrafluoropropene/vinylidene fluoride copolymers
View Patent ↗In accordance with the present invention, aqueous emulsion polymerization processes of synthesizing 2,3,3,3-tetrafluoropropene/vinylidene fluoride copolymers having 2,3,3,3-tetrafluoropropene as the major monomer unit are provided.
1. A process of synthesizing a copolymer consisting essentially of units derived from 2,3,3,3-tetrafluoropropene and vinylidene fluoride monomers, the process comprising the step of conducting an aqueous emulsion copolymerization of said monomers in the presence of a water soluble radical initiator to form the 2,3,3,3-tetrafluoropropene/vinylidene fluoride copolymer wherein the 2,3,3,3-tetrafluoropropene/vinylidene fluoride copolymer has a monomer molar unit ratio of 2,3,3,3-tetrafluoropropene/vinylidene fluoride between about 80/20 and about 99/1, wherein the copolymerization is carried out at a temperature from about 55° C. to about 70° C. and wherein the amount of said water soluble radical initiator is less than 1 wt % based on the weight of all the monomers in the copolymerization and is sufficiently low to produce a yield of copolymer of at least about 60%.
2. The process of claim 1 , wherein the monomers consist of 2,3,3,3-tetrafluoropropene and vinylidene fluoride.
3. The process of claim 1 , wherein the water soluble radical initiator is selected from the group consisting of Na 2 S 2 O 8 , K 2 S 2 O 8 , (NH 4 ) 2 S 2 O 8 , Fe 2 (S 2 O 8 ) 3 , K 2 S 2 O 8 /FeSO 4 , (NH 4 ) 2 S 2 O 8 /FeSO 4 , and combinations of two or more of these.
4. The process of claim 1 , wherein the involved water soluble radical initiator is added into the copolymerization in multiple portions and at spaced apart times during the reaction.
5. The process of claim 4 , wherein the involved water soluble radical initiator is added into the copolymerization in two or three portions and at two or three different times during the reaction.
6. The process of claim 5 , wherein the involved water soluble radical initiator is added into the copolymerization at a first time when the reaction is at a first reaction temperature and again at a second, later time when the reaction is at a second reaction temperature different than said first reaction temperature.
7. A process of synthesizing a copolymer consisting essentially of units derived from 2,3,3,3-tetrafluoropropene and vinylidene fluoride monomers, the process comprising the step of conducting an aqueous emulsion copolymerization of said monomers in the presence of a water soluble radical initiator to form the 2,3,3,3-tetrafluoropropene/vinylidene fluoride copolymer, wherein the 2,3,3,3-tetrafluoropropene/vinylidene fluoride copolymer has a monomer molar unit ratio of 2,3,3,3-tetrafluoropropene/vinylidene fluoride between about 80/20 and about 99/1 and wherein the water soluble radical initiator is added into the copolymerization at multiple times and the total amount is less than 1 wt % based on the weight of all the monomers in the copolymerization.
8. The process according to claim 7 , wherein the monomers consist of 2,3,3,3-tetrafluoropropene and vinylidene fluoride.
9. The process of claim 7 , wherein the water soluble radical initiator is selected from the group consisting of Na 2 S 2 O 8 , K 2 S 2 O 8 , (NH 4 ) 2 S 2 O 8 , Fe 2 (S 2 O 8 ) 3 , K 2 S 2 O 8 /FeSO 4 , (NH 4 ) 2 S 2 O 8 /FeSO 4 and combinations of two or more of these.
10. The process of claim 7 , wherein the involved water soluble radical initiator is added into the copolymerization in multiple portions and at spaced apart times during the reaction.
11. The process of claim 10 , wherein the water soluble radical initiator is added into the copolymerization at a first time when the reaction is at a first reaction temperature and again at a second, later time when the reaction is at a second reaction temperature different than said first reaction temperature.
12. The process of claim 10 ,
wherein a first water soluble radical initiator is added into the copolymerization at a first time,
wherein a second water soluble radical initiator is added into the copolymerization at a second time which is different from said first time, and
wherein said first water soluble radical initiator is different from said second water soluble radical initiator.
13. The process of claim 7 , wherein the amount of said water soluble radical initiator is sufficiently low to produce a yield of copolymer of at least about 60%.
14. The process of claim 7 , wherein the amount of said water soluble radical initiator is sufficiently low to produce a yield of copolymer of at least about 60%.
15. The process of claim 9 , wherein the amount of said water soluble radical initiator is sufficiently low to produce a yield of copolymer of at least about 60%.
16. The process of claim 10 , wherein the amount of said water soluble radical initiator is sufficiently low to produce a yield of copolymer of at least about 60%.
17. The process of claim 11 , wherein the amount of said water soluble radical initiator is sufficiently low to produce a yield of copolymer of at least about 60%.
18. The process of claim 12 , wherein the amount of said water soluble radical initiator is sufficiently low to produce a yield of copolymer of at least about 60%.