Method and composition for ink jet printing on a nonabsorbent substrate
Ink jet printing on a non-absorbent substrate involves a wet primer having a primer viscosity. The wet primer is applied on the non-absorbent substrate. An ink jet ink having an ink jet viscosity lower than the primer viscosity is jetted over the wet primer while the primer is still wet. The wet primer and ink are simultaneously cured on the substrate.
1. A method, comprising:
applying a layer of a primer onto a surface of a nonabsorbent substrate, wherein the primer has a corresponding viscosity, and wherein the nonabsorbent substrate comprises a metal;
ink jet printing an image by jetting drops of an ink jet ink over the primer layer while the primer is still wet, wherein the ink jet ink has a viscosity that is lower than the viscosity of the primer, wherein the ink jet ink solvates the primer, wherein the solvation of the primer by the ink jet ink prevents coalescence of the ink jet drops on the nonabsorbent substrate, and wherein the primer partially immobilizes the ink jet drops to facilitate adherence of the ink jet drops; and
while maintaining a constant temperature above 30 degrees Celsius, simultaneously curing the layer of primer and the ink jet ink on the nonabsorbent substrate.
2. The method of claim 1 , wherein the layer of primer is applied using a flexographic process.
3. The method of claim 1 , wherein the applied layer of primer is evenly applied onto the surface of the nonabsorbent substrate.
4. The method of claim 1 , wherein the applied layer of primer has a substantially consistent thickness across the substrate.
5. The method of claim 1 , wherein the cured inkjet ink is immobilized.
6. The method of claim 1 , wherein the viscosity of the primer is from 140 to 150 centipoises.
7. The method of claim 1 , wherein the primer is applied at a temperature of from 20 degree Celsius to 40 degree Celsius.
8. The method of claim 1 , wherein the applied primer layer has a film weight of 2 to 6 g/m 2 .
9. The method of claim 1 , wherein the viscosity of the inkjet ink is from about 5 to about 100 centipoises.
10. The method of claim 1 , wherein the simultaneous curing of the primer and the ink jet ink is performed with any of actinic radiation, thermal energy, or both actinic radiation and thermal energy.
11. The method of claim 1 , wherein the surface of the nonabsorbent substrate is a roughened surface having any of craters or pits, and wherein the primer settles into the craters or pits without absorption into the nonabsorbent substrate.
12. The method of claim 1 , wherein the nonabsorbent substrate is a metallic sheet, the method further comprising:
shaping the metallic sheet after the curing to form a product.
13. The method of claim 12 , wherein the formed product is any of metal can, signage, a decorative label or decal, an automotive component, or a computer component.
14. The method of claim 1 , wherein the partial immobilization of the ink jet drops allows the ink jet drops to spread from their deposition point without distorting a resultant image.
15. The method of claim 1 , wherein the partial immobilization of the ink jet drops prevents any of run-off or ink defects in the ink jet ink.
16. A method, comprising:
applying a layer of a primer onto a surface of a nonabsorbent substrate, wherein the primer has a corresponding viscosity, a surface energy of the primer being 20 milliNewtons to 50 milliNewtons, and the primer includes:
a curable epoxy resin; and
a monomer with a surface tension of 28.5 dynes/cm to 32 dynes/cm;
ink jet printing an image by jetting drops of an ink jet ink drops of an ink jet ink over the primer layer while the primer is still wet, wherein solvation of the primer by the ink iet ink prevents coalescence of the ink iet drops on the nonabsorbent substrate, wherein the ink jet ink has a viscosity that is lower than the viscosity of the primer and the ink jet ink includes:
a monofunctional or a polyfunctional monomer; and
a pigment from 0.5% to 30% by weight of the ink jet ink; and
while maintaining a constant temperature above 30 degrees Celsius, simultaneously curing the layer of primer and the ink jet ink on the nonabsorbent substrate.