Extrusion coating of low density polyethylene and heat-sealed article made therefrom
The present invention relates to the use of a at least a part of a polymer layer comprising a composition (Co), the composition comprising a low density polyethylene (LDPE) produced in a tubular reactor which composition is free of additives as a thermoplastic surface of an extrusion coated structure comprising the polymer layer and a first substrate for preparing heat-sealed articles by heat-sealing of said thermoplastic surface with a second substrate; and The use of a at least a part of a polymer layer comprising a composition (Co), the composition comprising a low density polyethylene (LDPE) having a melt flow rate (MFR) according to ISO 1133 (190° C., 2.16 kg) higher than 3.0 g/10 min; a molecular weight distribution Mw/Mn which is greater than 10; and a vinylidene content which is at least 15/100 k C; which composition is free of additives as a thermoplastic surface of an extrusion coated structure comprising the polymer layer and a first substrate for preparing heat-sealed articles by heat-sealing of said thermoplastic surface with a second substrate.
1. An article including a thermoplastic surface heat-sealed onto a second substrate, wherein said thermoplastic surface is at least a part of a polymer layer comprising a composition (Co) comprising a low density homopolymer of ethylene (LDPE homopolymer),
wherein the polymer layer is free of additives,
whereby the polymer layer is one layer of a coated structure further comprising a first substrate whereby the polymer layer is extrusion coated onto the first substrate prior to heat-sealing, wherein heat-sealing is done by applying heat to the thermoplastic surface and the second substrate to soften or melt the thermoplastic surface and the second substrate while applying pressure where the thermoplastic surface and the second substrate are to be joined,
wherein the thermoplastic surface has been heat-sealed onto the second substrate by a process comprising the following steps in the given order:
a) preparing a low density homopolymer of ethylene (LDPE homopolymer);
a1) wherein the low density homopolymer of ethylene (LDPE homopolymer) is produced in a tubular reactor and
a2) wherein the low density homopolymer of ethylene (LDPE homopolymer) has:
i) a melt flow rate (MFR) according to ISO 1133 (190° C., 2.16 kg) higher than 3.0 g/10 min;
ii) a molecular weight distribution Mw/Mn which is greater than 10, and
iii) a vinylidene content which is at least 15 / 100k C;
b) preparing a composition (Co) comprising low density homopolymer of ethylene (LDPE homopolymer) obtained in step a), wherein the low density polyethylene (LDPE) is the only polymer in the composition (Co); and
c) extrusion coating a polymer layer comprising at least 95 wt.% of the composition obtained in step onto a first substrate;
whereby no additives are present in the composition or added to the composition or any of its ingredients before or during steps a) to b) are effected; and
d) heat-sealing a first thermoplastic surface which is at least a part of the polymer layer obtained in step c) with a second substrate.
2. The article of claim 1 , wherein step c) is carried out at a temperature of 275 to 330° C.
3. The article of claim 1 , wherein step d) is carried out at a temperature of 100 to 200° C.