Plated steel sheet for hot press forming having excellent weldability and corrosion resistance, forming member, and manufacturing method thereof
The present invention relates to a plated steel sheet for hot press forming, a hot-press forming member manufactured using the same, and a manufacturing method thereof. The plated steel sheet comprises: a base steel sheet and a composite plated layer that is formed on at least one surface of the base steel sheet, and has a Mn-based plated layer and an Al-based plated layer alternately formed therein, an Al-based plated layer being formed on the uppermost layer thereof, wherein the composite plated layer has a total thickness of 5 to 30 μm, and in this case, the Mn-based plated layer accounts for 5 to 60% of the total thickness.
1. A plated steel sheet comprising:
a base steel sheet; and
a composite plating layer formed on at least one side of the base steel sheet, the composite plating layer comprising a Mn-based plating layer and an Al-based plating layer alternately formed with the Al-based plating layer being an upper most layer,
wherein the composite plating layer has a total thickness of 5 μm to 30 μm, and the Mn-based plating layer has a thickness accounting for 5% to 60% of the total thickness of the composite plating layer, and
wherein the Mn-based plating layer comprises at least one selected from the group consisting of chromium (Cr), zinc (Zn), beryllium (Be), magnesium (Mg), calcium (Ca), and titanium (Ti) in an amount of 5 wt % to 20 wt %.
2. The plated steel sheet of claim 1 , wherein the composite plating layer has a total thickness of 5 μm to 25 μm, and the Mn-based plating layer has a thickness accounting for 20% to 50% of the total thickness of the composite plating layer.
3. The plated steel sheet of claim 1 , wherein the Al-based plating layer comprises at least one selected from the group consisting of zinc (Zn), silicon (Si), magnesium (Mg), and manganese (Mn) in an amount of 20 wt % or less, excluding 0 wt %.
4. The plated steel sheet of claim 1 , wherein the plated steel sheet is for hot press forming (HPF).