Ultrahigh-strength gas metal arc welded joint having excellent impact toughness, and solid wire for producing same
Provided is an ultrahigh-strength gas metal arc welded joint having a high degree of impact toughness. The ultrahigh-strength gas metal arc welded joint comprises, by wt %, carbon (C): 0.05% to 0.1%, silicon (Si): 0.2% to 0.7%, manganese (Mn): 1.5% to 2.5%, nickel (Ni): 2.0% to 3.5%, chromium (Cr): 0.3% to 0.9%, copper (Cu): 0.1% to 0.3%, molybdenum (Mo): 0.5% to 0.8%, titanium (Ti): 0.02% to 0.04%, boron (B): 0.002% to 0.005%, aluminum (Al): 0.001% to 0.03%, nitrogen (N): 0.002% to 0.007%, phosphorus (P): 0.03% or less, sulfur (S): 0.03% or less, oxygen (O): 0.02% to 0.05%, and a balance of iron (Fe) and other inevitable impurities, satisfying 0.4≤Ti/O≤1.2., 2.8≤Ti/N≤9.0, 10≤(2Ti+5B)/N≤20, and 3.5≤Mn+2Cr+3Mo+3Cu≤7.5.
1. An ultrahigh-strength gas metal arc welded joint having a high degree of impact toughness, the ultrahigh-strength gas metal arc welded joint comprising, by wt %, carbon (C): 0.05% to 0.1%, silicon (Si): 0.2% to 0.7%, manganese (Mn): 1.5% to 2.5%, nickel (Ni): 2.0% to 3.5%, chromium (Cr): 0.3% to 0.9%, copper (Cu): 0.1% to 0.3%, molybdenum (Mo): 0.5% to 0.8%, titanium (Ti): 0.02% to 0.04%, boron (B): 0.002% to 0.005%, aluminum (Al): 0.001% to 0.03%, nitrogen (N): 0.002% to 0.007%, phosphorus (P): 0.03% or less, sulfur (S): 0.03% or less, oxygen (O): 0.02% to 0.05%, and a balance of iron (Fe) and other inevitable impurities,
wherein contents of titanium (Ti) and oxygen (O) satisfy Formula 1 below, contents of titanium (Ti) and nitrogen (N) satisfy Formula 2 below, contents of titanium (Ti), boron (B), and nitrogen (N) satisfy Formula 3 below, and contents of manganese (Mn), chromium (Cr), molybdenum (Mo), and copper (Cu) satisfy Formula 4 below,
wherein the ultrahigh-strength gas metal arc welded joint has a microstructure comprising acicular ferrite in an area fraction of 20% to 30% and bainite in an area fraction of 70% to 80%, and
wherein a composite oxide, TiO-TiN, having an average particle diameter of 0.01 μm to 0.10 μm is distributed in the ultrahigh-strength gas metal arc welded joint at a density of 1×10 8 or more particles per mm 3 ,
0.4≤Ti/O≤1.2 [Formula 1]
2.8≤Ti/N≤9.0 [Formula 2]
10≤(2Ti+5B)/N≤20 [Formula 3]
3.5≤Mn+2Cr+3Mo+3Cu≤7.5 [Formula 4].
2. The ultrahigh-strength gas metal arc welded joint of claim 1 , further comprising, by wt %, at least one of niobium (Nb): 0.001% to 0.1% and vanadium (V): 0.005% to 0.1%, and at least one of calcium (Ca): 0.0005% to 0.005% and a rare earth metal (REM): 0.005% to 0.05%.
3. The ultrahigh-strength gas metal arc welded joint of claim 1 , wherein particles of the composite oxide, TiO-TiN, are distributed at intervals of 50 μm or less.
4. The ultrahigh-strength gas metal arc welded joint of claim 1 , wherein the ultrahigh-strength gas metal arc welded joint has impact toughness of 47 J or greater at −20° C.