Process for producing a cured rubber sheet that is free of surface particulate

1. A method for making a cured rubber sheet, the method comprising:

i. providing an uncured rubber sheet, where the uncured rubber sheet includes opposing planar surfaces;

ii. applying a curable coating composition to one planar surface of the sheet to form a layer of curable coating composition;

iii. subjecting the curable coating composition to curing conditions that cure the coating composition and thereby form a cured coating layer on the uncured rubber sheet;

iv. rolling the uncured rubber sheet having a cured coating layer onto itself to form a roll; and

v. subjecting the roll to curing conditions that cure the uncured rubber sheet and thereby forms a roll of cured rubber sheet;

where the method is devoid of a step of applying a particulate to a planar surface of the sheet prior to said step of subjecting the roll to curing conditions that cures the uncured rubber sheet.

2. The method of claim 1 , where the uncured rubber is uncured EPDM, and said method produces a cured EPDM sheet.

3. The method of claim 1 , further comprising the step of unrolling the roll of cured rubber sheet after said step of subjecting the roll to curing conditions.

4. The method of claim 1 , where said step of providing an uncured rubber sheet includes calendering an uncured EPDM composition into a sheet.

5. The method of claim 1 , where the uncured rubber sheet has a thickness of from about 30 mil to about 120 mil, and where said step of applying includes forming a curable coating layer having a thickness of from about 0.1 μm to about 10 μm.

6. The method of claim 1 , where the curable coating composition is curable by electromagnetic radiation.

7. The method of claim 1 , where said cured rubber sheet includes less than 20 g/m 2 of surface particulate.

8. The method of claim 1 , where the curable coating composition is curable by UV light.

9. The method of claim 8 , where the curable coating composition includes UV-curable monomer, or UV-curable oligomer.

10. The method of claim 9 , where the UV-curable monomer or UV-curable oligomer includes at least 1 acrylate functionality.

11. The method of claim 1 , where the curable coating composition includes a cure promoter.

12. The method of claim 1 , where said step of subjecting the curable coating to curing conditions includes subjecting the curable coating to electromagnetic radiation.

13. The method of claim 12 , where the electromagnetic radiation is UV light.

14. The method of claim 1 , where said step of subjecting the curable coating composition to curing conditions substantially cures the coating composition.

15. The method of claim 1 , where said step of subjecting the curable coating composition to curing conditions fully cures the coating composition.

16. The method of claim 1 , where said step of subjecting the roll to curing conditions includes subjecting the roll to a temperature of at least 130° C.

17. The method of claim 1 , where said step of subjecting the roll to curing conditions includes placing the roll into an autoclave.

18. The method of claim 3 , where said step of unrolling the roll includes stripping.

19. A cured rubber membrane sheet comprising:

i. a planar body having first and second planar surfaces, said planar body including cured rubber; and

ii. a cured coating layer disposed on said first planar surface, where said first and second planar surfaces and said cured coating layer are substantially free of surface particulate, where said first planar surface includes a first lap-edge region, and where said first lap-edge region is substantially free of said cured coating.

20. The membrane of claim 19 , where the cured rubber includes cured EPDM.

21. The membrane of claim 19 , where the planar body has a thickness of from about 30 to about 120 mil.

22. The membrane of claim 19 , where said cured coating has a thickness of from about 0.1 μm to about 10 μm.

23. The membrane of claim 19 , where said cured coating is a release coating.

24. The membrane of claim 19 , where said rubber membrane includes less than 20 g/m 2 of surface particulate.

25. The membrane of claim 19 , where said rubber membrane includes less than 0.1 g/m 2 of surface particulate.