Automobile part and method for manufacturing automobile part
[Object] There are provided automobile parts and a method for manufacturing the automobile parts. The automobile parts have an excellent corrosion resistance after coated with a electrodeposition paint with smaller thickness, improve formability and productivity in hot pressing, and also improve chemical conversion treatability after hot press-forming. [Solution] An automobile part according to the present invention includes: a formed steel sheet having an intermetallic compound layer formed on a surface of the steel sheet, the intermetallic compound layer being formed of Al—Fe intermetallic compound having a thickness of 10 μm or more and 50 μm or less, the intermetallic compound layer including a diffusion layer positioned in closest proximity to the steel sheet, the diffusion layer having a thickness of 10 μm or less; a surface coating layer provided on a surface of the intermetallic compound layer, the surface coating layer including a coating containing ZnO and a zinc phosphate coating and having a surface roughness of 3 μm or more and 20 μm or less as a maximum profile height Rt in accordance with JIS B0601 (2001); and an electrodeposition paint film provided on a surface of the surface coating layer and having a thickness of 6 μm or more and less than 15 μm.
1. An automobile part, comprising:
a formed steel sheet having an intermetallic compound layer formed on a surface of the steel sheet, the intermetallic compound layer, being formed of Al—Fe intermetallic compound having a thickness of 10 μm or more and 50 μm or less, the intermetallic compound layer including a diffusion layer positioned in closest proximity to the steel sheet, the diffusion layer having a thickness of 10 μm or less;
a surface coating layer provided on a surface of the intermetallic compound layer, the surface coating layer including a coating containing ZnO and a zinc phosphate coating and having a surface roughness of 3 μm or more and 20 μm or less as a maximum profile height Rt in accordance with JIS B0601 (2001); and
an electrodeposition paint film provided on a surface of the surface coating layer and having a thickness of 6 μm or more and less than 15 μm,
wherein the steel sheet is an Al plated steel sheet having an Al plating layer formed on a surface of the steel sheet serving as a base metal, and
wherein the Al plating layer has an average primary crystal diameter of 4 μm or more and 40 μm or less before hot pressing.
2. The automobile part according to claim 1 , wherein the maximum profile height Rt is 7 μm or more and 14 μm or less.
3. The automobile part according to claim 1 , wherein a content of ZnO is 0.3 g/m 2 or more and 3 g/m 2 or less in metallic Zn equivalent for one surface.
4. The automobile part according to claim 1 , wherein an amount of the Al plating layer is 30 g/m 2 or more and 110 g/m 2 or less for one surface.
5. The automobile part according to claim 1 , wherein the ZnO has an average grain size of 50 μm or more and 1000 nm or less in diameter.
6. The automobile part according to claim 5 , wherein a content of ZnO is 0.3 g/m 2 or more and 3 g/m 2 or less in metallic Zn equivalent for one surface.
7. The automobile part according to claim 6 , wherein an amount of the Al plating layer is 30 g/m 2 or more and 110 g/m 2 or less for one surface.