Methods and systems for increasing surface smoothness of three-dimensional printed article
Technologies are generally described to increase a surface smoothness of a 3D printed article implementing a water-based treatment using layer by layer (LBL) deposition. An initial 3D printed article having an anionic surface may be treated with a first aqueous solution comprising at least one polycation that may bind to the anionic surface to produce a first treated surface, which may be rinsed with water to remove the first aqueous solution. The first treated surface may be treated with a second aqueous solution comprising at least one anionic microparticle that may bind to the polycation to produce a final 3D printed article having a second treated surface, which may be rinsed with water to remove the second aqueous solution. The bound polycation and anionic microparticle may be present as a single layer in the final 3D printed article that may act as a conformal coating to increase the surface smoothness.
1. A method to treat a surface of an initial three-dimensional (3D) printed article, the method comprising:
providing the initial 3D printed article that has an anionic surface;
treating the anionic surface with a first aqueous solution for a time period based on a first concentration of the first aqueous solution, wherein the first aqueous solution includes at least one polycation to produce a first treated surface; and
treating the first treated surface with a second aqueous solution for another time period based on a second concentration of the second aqueous solution, wherein the second aqueous solution includes at least one anionic microparticle to produce a final 3D printed article that has a second treated surface;
wherein:
the polycation binds to the anionic surface; and
the anionic microparticle binds to the polycation.
2. The method of claim 1 , wherein the polycation is present in the final 3D printed article as a single layer that has thickness such that a smoothness of the surface of the final 3D printed article is higher than a smoothness of the surface of the initial 3D article.
3. The method of claim 1 , further comprising:
heating the final 3D printed article to a temperature above a glass transition temperature (T g ) of the anionic microparticle.
4. The method of claim 3 , wherein the surface of the final 3D printed article has a higher smoothness after the heating step than immediately before the heating step.
5. The method of claim 1 , further comprising:
adding at least one titania particle, at least one polyionic dye, or both to the second aqueous solution prior to the second treatment step.
6. The method of claim 5 , wherein the polyionic dye is a porphyrin dye or a phthalocyanine dye.
7. The method of claim 1 , further comprising:
adding at least one silica particle to the second aqueous solution prior to the second treatment step.
8. The method of claim 7 , wherein the final 3D printed article has a scratch resistance that is higher than a substantially identical final 3D printed article made without an addition of the at least one silica particle.