Negative electrode active material, negative electrode and battery
Provided is a negative electrode active material that can improve the discharge capacity per volume and charge-discharge cycle characteristics. The negative electrode active material of the present embodiment includes a powder material and an oxide layer. The powder material contains an alloy phase which undergoes thermoelastic diffusionless transformation when releasing metal ions or occluding the metal ions. The oxide layer is formed on the surface of the powder material, and has a thickness of not more than 10 nm.
1. A negative electrode active material, comprising:
a powder material containing an alloy phase which undergoes thermoelastic diffusionless transformation when releasing metal ions or occluding the metal ions; and
an oxide layer which is formed on the surface of the powder material, and has a thickness of not more than 10 nm,
wherein the alloy phase contains a crystal structure which is DO 3 in Strukturbericht notation,
wherein the alloy phase undergoes thermoelastic diffusionless transformation when occluding the metal ions and undergoes reverse transformation when releasing the metal ions,
wherein the alloy phase after the thermoelastic diffusionless transformation contains a crystal structure which is 2H in Ramsdell notation, and
wherein the alloy phase after the reverse transformation contains a crystal structure which is DO 3 in Strukturbericht notation.
2. The negative electrode active material according to claim 1 , wherein
an atomic content of oxygen is not more than 70 at % in the oxide layer.
3. The negative electrode active rnaterial according to claim 2 , wherein
the alloy phase ins Cu and Sn.
4. The negative electrode active material according to claim 3 , wherein
the alloy phase contains 10 to 20 at % or 21 to 27 at % of Sn, with the balance being Cu and impurities.
5. The negative electrode active material according to claim 3 , wherein
the alloy phase contains, in place of a part of Cu, one or more selected from the group consisting of Ti, V, Cr, Mn, Fe, Co, Ni, Zn, Al, Si, B, and C.
6. The negative el rode active material according to claim 5 , wherein
the alloy phase contains:
Sn: 10 to 35 at %; and
one or more selected from the group consisting of Ti: 9.0 at % or less, V: 49.0 at % or less, Cr: 49.0 at % or less, Mn: 9.0 at % or less, Fe: 49,0 at % or less, Co: 49.0 at % or less, Ni: 9.0 at % or less, Zn: 29.0 at % or less, Al: 49.0 at % or less, Si: 49.0 at % or less, B: 5.0 at % or less, and C: 5.0 at % or less,
with the balance being Cu and impurities.
7. The negative electrode active material according to claim 1 , wherein
the alloy phase contains Cu and Sn.
8. A negative electrode, comprising he negative electrode active material according to claim 1 .
9. A battery, comprising the negative electrode according to claim 8 .
10. A negative electrode active material, comprising:
powder material containing an alloy phase which contains 10 to 20 at % of Sn, with the balance being Cu and impurities; and
an oxide layer which is formed on the surface of the powder material, and has a thickness of not more than 10 nm, wherein the oxide layer consists of constituting elements of the powder material, and oxygen.
11. A negative electrode active material comprising:
powder material containing an alloy phase which contains: Sn: 10 to 20 at %; and one or more selected from the group consisting of Ti: 9.0 at % or less, V: 49.0 at % or less, Cr: 49.0 at % or less, Mn: 9.0 at % or less, Fe: 49.0 at % or less, Co: 49.0 at % or less, Ni: 9.0 at % or less, Zn: 29.0 at % or less, Al: 49.8 at % or less, Si: 49.0 at % or less, B: 5.0 at % or less, and C: 5.0 at % or less, with the balance being Cu and impurities; and
an oxide layer which is formed on the surface of the powder material, and has a thickness of not more than 10 nm wherein the oxide layer consists of constituting elements of the powder material and oxygen.