Oxynitride phosphor powder and method for producing same
An oxynitride phosphor powder has a fluorescence peak wavelength of 587 to 630 nm and a high external quantum efficiency. A method of producing the oxynitride phosphor powder containing Li at 50 to 10,000 ppm includes mixing silicon nitride powder, a substance serving as an aluminum source, a substance serving as a calcium source and a substance serving as an europium source; firing the mixture at 1500 to 2000° C. in an inert gas atmosphere or a reducing gas atmosphere to obtain a fired oxynitride phosphor composed mainly of Ca-containing α-SiAlON, as an intermediate; and heat treating the fired oxynitride phosphor at a temperature of 1450° C. to less than the firing temperature, in an inert gas atmosphere or in a reducing gas atmosphere in the presence of Li.
1. A method of producing an oxynitride phosphor powder containing Li at 50 to 10,000 ppm, comprising:
mixing silicon nitride powder, a substance serving as an aluminum source, a substance serving as a calcium source and a substance serving as an europium source to form a mixture;
firing the mixture at 1500 to 2000° C. in an inert gas atmosphere or in a reducing gas atmosphere to obtain a fired oxynitride phosphor composed mainly of Ca-containing α-SiAlON not containing Li, as an intermediate; and
heat treating the fired oxynitride phosphor at a temperature of 1450° C. to less than the firing temperature, in an inert gas atmosphere or in a reducing gas atmosphere in the presence of Li.
2. An oxynitride phosphor powder obtained by mixing silicon nitride powder, a substance serving as an aluminum source, a substance serving as a calcium source and a substance serving as an europium source to form a mixture, firing the mixture at 1500 to 2000° C. in an inert gas atmosphere or in a reducing gas atmosphere to obtain a fired oxynitride phosphor composed mainly of Ca-containing α-SiAlON not containing Li, as an intermediate, and heat treating the fired oxynitride phosphor at a temperature of 1450° C. to less than the firing temperature, in an inert gas atmosphere or in a reducing gas atmosphere in the presence of Li, the powder containing 50 to 10,000 ppm of Li and having a surface Li content of 50% or greater.
3. An oxynitride phosphor powder comprising Ca-containing α-SiAlON and aluminum nitride, and 50 to 10,000 ppm of Li and having a surface Li content of 50% or greater.
4. The oxynitride phosphor powder according to claim 3 , wherein a compositional formula of the Ca-containing α-SiAlON and aluminum nitride is as follows:
Ca x1 EU x2 Si 12−(y+z) Al (y+z) O z N 16−z
wherein 1.60≤x1+x2≤3.00, 0.10≤x2/x1≤1.20, 4.0≤y≤7.0, 0≤z≤0.5.
5. The oxynitride phosphor powder according to claim 4 , wherein the aluminum nitride content is greater than 0 mass % and less than 36 mass %.
6. The oxynitride phosphor powder according to claim 4 , wherein excitation with light having a wavelength of 450 nm causes emission of fluorescence with a peak wavelength in a wavelength range of 605 nm to 630 nm, an external quantum efficiency thereof being 50% or greater.
7. The oxynitride phosphor powder according to claim 3 , wherein the aluminum nitride content is greater than 0 mass % and less than 36 mass %.
8. The oxynitride phosphor powder according to claim 7 , wherein excitation with light having a wavelength of 450 nm causes emission of fluorescence with a peak wavelength in a wavelength range of 605 nm to 630 nm, an external quantum efficiency thereof being 50% or greater.
9. The oxynitride phosphor powder according to claim 3 , wherein excitation with light having a wavelength of 450 nm causes emission of fluorescence with a peak wavelength in a wavelength range of 605 nm to 630 nm, an external quantum efficiency thereof being 50% or greater.
10. An oxynitride phosphor powder obtained by mixing silicon nitride powder, a substance serving as an aluminum source, a substance serving as a calcium source and a substance serving as an europium source to form a mixture, firing the mixture at 1500 to 2000° C. in an inert gas atmosphere or in a reducing gas atmosphere to obtain a fired oxynitride phosphor comprising Ca-containing α-SiAlON not containing Li and aluminum nitride, as an intermediate, and heat treating the fired oxynitride phosphor at a temperature of 1450° C. to less than the firing temperature, in an inert gas atmosphere or in a reducing gas atmosphere in the presence of Li, the powder containing 50 to 10,000 ppm of Li and having a surface Li content of 50% or greater.
11. A light-emitting device employing the oxynitride phosphor powder according to claim 10 .
12. A light-emitting device employing the oxynitride phosphor powder according to claim 3 .
13. A light-emitting device employing the oxynitride phosphor powder according to claim 4 .
14. A light-emitting device employing the oxynitride phosphor powder according to claim 7 .
15. A light-emitting device employing the oxynitride phosphor powder according to claim 9 .
16. A light-emitting device employing the oxynitride phosphor powder according to claim 10 .