Methyl methacrylate vinylaromate copolymers

1. A copolymer consisting of the following monomers:

(A) 30-45% (w/w) of methyl methacrylate (MMA);

(B) 55-70% (w/w) of one or more vinylaromatic(s); and optionally

(C) 0-1% (w/w) of one or more aliphatic vinyl(s),

wherein said copolymer is a random copolymer and has a melt flow index determined at a temperature of 200° C. and at a load of 5 kg according to ASTM procedure D1238 of less than 20 g/10 min and comprises at least 500 consecutive monomer moieties.

2. The copolymer according to claim 1 , wherein the one or more vinylaromatic(s) (B) comprise(s) styrene, one or more styrene derivative(s) or a mixture thereof.

3. The copolymer according to claim 1 , wherein the one or more vinylaromatic(s) (B) comprise(s) at least 50% (w/w) styrene.

4. The copolymer according to claim 1 , which is a random copolymer, consisting of:

(A) 30-45% (w/w) of methyl methacrylate (MMA); and

(B) 55-70% (w/w) of one or more vinylaromatic(s).

5. A polymer composition comprising a copolymer according to claim 1 and at least one further thermoplastic polymer component.

6. The polymer composition according to claim 5 , further comprising one or more thermoplastic polymer(s) selected from the group consisting of:

polystyrene, poly(meth)acrylate, polycarbonate, styrene acrylonitrile copolymer (SAN), acrylonitrile butadiene styrene copolymer (ABS), acrylonitrile styrene acrylate copolymer (ASA), polylactic acid (PLA), polyester, polyoxymethylene, polyethylene, polypropylene, polyvinylchloride (PVC) and polyamide.

7. The copolymer according to claim 1 , wherein said copolymer is comprised in a product, wherein said product has a light transmission of at least 50% of ultraviolet (UV) light at a wavelength range of between 250 nm and 370 nm.

8. The copolymer according to claim 1 , wherein said copolymer is comprised in a product, wherein said product has a light transmission of at least 60% of ultraviolet (UV) light at a wavelength range of between 250 nm and 370 nm.

9. The copolymer according to claim 1 , wherein said copolymer is comprised in a product, wherein said product has a light transmission of at least 70% of ultraviolet (UV) light at a wavelength range of between 250 nm and 370 nm.

10. The copolymer according to claim 1 , wherein said copolymer is comprised in a product, wherein said product has a light transmission of at least 80% of ultraviolet (UV) light at a wavelength range of between 250 nm and 370 nm.

11. The copolymer according to claim 1 , wherein said copolymer is comprised in a product, wherein said product has a light transmission of at least 85% of ultraviolet (UV) light at a wavelength range of between 250 nm and 370 nm.

12. The copolymer according to claim 1 , wherein said copolymer is comprised in a product selected from the group consisting of thermoplastic molding, film material, packing material, fiber, yarn, fabric, tissue, foam and composite material.

13. The copolymer according to claim 1 , wherein the one or more vinylaromatic(s) (B) comprise(s) at least 70% (w/w) styrene.

14. The copolymer according to claim 1 , wherein the one or more vinylaromatic(s) (B) wherein the only vinylaromatic (B) in said copolymer is styrene.

15. The copolymer according to claim 1 , said copolymer enabling light transmittance in the visible spectrum and in the ultraviolet spectrum of between 250 nm and 800 nm.

16. A method for producing a copolymer according to claim 1 , wherein said method comprises the following steps:

(i) providing a reaction mixture comprising:

(a) one or more type(s) of methyl methacrylate (MMA) monomers,

(b) one or more type(s) vinylaromatic monomers, and optionally

(c) one or more type(s) aliphatic vinyl monomers, in a ratio of (a):(b):(c) resulting in a copolymer according to claim 1 ;

(ii) initiating the polymerization (a), (b) and optionally (c) in the reaction mixture of step (i);

(iii) enabling the copolymerization of (a), (b) and optionally (c) in said reaction mixture wherein the polymerization is initiated according to step (ii); and

(iv) withdrawing the copolymer from the reaction mixture wherein (a), (b) and optionally (c) have been copolymerized according to step (iii).

17. The method of claim 16 , wherein step (ii) comprises heating of the reaction mixture obtained from step (i) above a temperature above 100° C. or adding one or more polymerization initiator(s) to said reaction mixture.

18. The method of claim 16 , wherein step (ii) comprises heating of the reaction mixture obtained from step (i) above a temperature above 100° C. and adding one or more polymerization initiator(s) to said reaction mixture.