Welded joint and method of manufacturing welded joint
A welded joint having high strength and good hydrogen embrittlement resistance is provided. A welded joint is a welded joint obtained by welding a base material using a welding material. The base material has a chemical composition of, in mass %: C: 0.005 to 0.1%; Si: up to 1.2%; Mn: 2.5 to 6.5%; Ni: 8 to 15%; Cr: 19 to 25%; Mo: 0.01 to 4.5%; V: 0.01 to 0.5%; Nb: 0.01 to 0.5% Al: less than 0.05%; N: 0.15 to 0.45%; O: up to 0.02%; P: up to 0.05%; and S: up to 0.04%, and a balance being iron and impurities, and which satisfies Equation (1). The welding material has a chemical composition which satisfies Equations (1) and (2). Ni+0.65Cr+0.98Mo+1.05Mn+0.35Si+12.6C≥29 (1) 0.31C+0.048Si−0.02Mn−0.056Cr+0.007Ni−0.013Mo≤−1.0 (2)
1. A method of manufacturing a welded joint, comprising the steps of:
preparing a base material having a chemical composition of, in mass %:
C: 0.005 to 0.1%;
Si: up to 1.2%;
Mn: 2.5 to 6.5%;
Ni: 8 to 15%;
Cr: 19 to 25%;
Mo: 0.01 to 4.5%;
V: 0.01 to 0.5%;
Nb: 0.01 to 0.5%;
Al: less than 0.05%;
N: 0.15 to 0.45%;
O: up to 0.02%;
P: up to 0.05%; and
S: up to 0.04%, and
a balance being iron and impurities,
preparing a welding material having a chemical composition consisting of, in mass %:
C: 0.005 to 0.1%;
Si: up to 0.7%;
Mn: 0.5 to 3%;
Ni: 8 to 23%;
Cr: 17 to 25%;
Mo: 0.01 to 4%;
V: 0 to 0.5%;
Nb: 0 to 0.5%;
Al: less than 0.05%;
N: less than 0.15%;
O: up to 0.02%;
P: up to 0.03%; and
s: up to 0.02%, and
a balance being iron and impurities, and
welding the base material using the welding material,
wherein the chemical composition of the base material satisfies Equation (1), and the chemical composition of the welding material satisfies Equations (1) and (2),
Ni+0.65Cr+0.98Mo+1.05Mn+0.35Si+12.6C≥29 (1), and
0.31C+0.048Si−0.02Mn−0.056Cr+0.007Ni−0.013Mo≤−1.0 (2),
where the contents of elements (in mass %) are substituted for the symbols of these elements in Equations (1) and (2).
2. The method of manufacturing a welded joint according to claim 1 , wherein
the step of welding includes welding the base material using the welding material such that the welded joint has a surface excess weld metal height h (mm) that satisfies Equation (3),
1.9×(0.31C+0.048Si−0.02Mn−0.056Cr+0.007Ni−0.013Mo)+3 ≤h (3),
where the contents of the elements in the welding material (in mass %) are substituted for the symbols of these elements in Equation (3).
3. The method of manufacturing a welded joint according to claim 1 , wherein for Equation (2),
0.31C+0.048Si−0.02Mn−0.056Cr+0.007Ni−0.013Mo of is less than or equal to −1.3.
4. The method of manufacturing a welded joint according to claim 1 , wherein
the Cr content of the welding material is 17 to 24.6 mass %.
5. The method of manufacturing a welded joint according to claim 1 , wherein
the N content of the welding material is not higher than 0.13 mass %.