High strength stone plastic floor and manufacturing method thereof
The invention provides a high strength stone plastic floor and manufacturing method thereof. The stone plastic floor comprises a PVC substrate and a surface layer on a surface of the PVC substrate. Compositions of PVC substrate comprise: PVC powder from 20 to 35 weight percent, calcium carbonate from 60 to 70 weight percent, stabilizer from 1 to 3 weight percent, flexibilizer from 1 to 3 weight percent, lubricants from 0.4 to 1 weight percent, and colorant from 0.4 to 1 weight percent. The high strength stone plastic floor does not contain plasticizer so environmental risks are completely avoided. The contractility is good. The high strength stone plastic floor is resistant to high temperature and direct sunlight. Compared with conventional stone plastic floor, lifespan of the present invention is prolonged. The PVC substrate of the floor can be combined with different layers and can integrate different advantages of other floors.
1. A high strength stone plastic floor comprising a PVC substrate and a surface layer on a surface of the PVC substrate; wherein compositions of the PVC substrate comprise: PVC powder from 20 to 35 weight percent, calcium carbonate from 60 to 70 weight percent, stabilizer from 1 to 3 weight percent, flexibilizer from 1 to 3 weight percent, lubricants from 0.4 to 1 weight percent, and colorant from 0.4 to 1 weight percent, wherein the high strength stone plastic floor does not contain plasticizer.
2. The high strength stone plastic floor as claimed in claim 1 , wherein the surface layer comprises two layers: a color film layer and a wear-resistant layer set successively on the PVC substrate.
3. The high strength stone plastic floor as claimed in claim 2 , wherein the thickness of the PVC substrate is 2.0-8.0 mm; the thickness of the color film is 0.05-0.09 mm; the thickness of the wear-resistant layer is 0.07-1.0 mm.
4. The high strength stone plastic floor as claimed in claim 1 , wherein the surface layer is a PVC wear-resistant layer.
5. The high strength stone plastic floor as claimed in claim 1 , wherein the surface layer is a fire-proof board layer.
6. The high strength stone plastic floor as claimed in claim 1 , wherein the surface layer is a wood veneer layer.
7. A manufacturing method of the high strength stone plastic floor as claimed in claim 1 comprises the following steps:
providing materials to manufacture PVC substrate: PVC powder from 20 to 35 weight percent, calcium carbonate from 60 to 70 weight percent, stabilizer from 1 to 3 weight percent, flexibilizer from 1 to 3 weight percent, lubricants from 0.4 to 1 weight percent, colorant from 0.4 to 1 weight percent;
mixing and stirring the above materials;
extruding and calendaring the above materials to get sheet by extruder;
cooling to get the PVC substrate;
laminating the PVC substrate and surface layer to form the stone plastic floor.
8. The manufacturing method of the high strength stone plastic floor as claimed in claim 7 , wherein, in the stirring step, the speed of stirring is 1000-3000 r/min and time of stirring is 4-8 minutes.
9. The manufacturing method of the high strength stone plastic floor as claimed in claim 7 , wherein, in the extruding step, the temperature is 187-210° C.