Compositions and methods for manufacturing blow molded containers
Blow molded containers and methods for making the same are provided. A blow molded container has a container wall including a thermoplastic polymer material having a rheology melt strength (R ms ) of at least 30 Pa·s 2 . A method of making a container includes providing a material sheet including at least one thermoplastic polymer layer having a rheology melt strength (R ms ) of at least 30 Pa·s 2 , forming the material sheet into a tube, sealing the tube at a seal area, and blow molding the tube to form a container.
1. A blow molded container, comprising:
a container wall comprising a thermoplastic polymer material having a rheology melt strength (R ms ) of at least 30 Pa·s 2 ,
wherein the material comprises:
(i) a blend of a high melt strength polypropylene and a low melt strength polypropylene,
(ii) a blend of a low melt strength polypropylene and a high density polyethylene, or
(iii) a blend of a high melt strength polypropylene and a high density polyethylene.
2. The container of claim 1 , wherein the material comprises the blend of the high melt strength polypropylene and the low melt strength polypropylene, the high melt strength polypropylene has a rheology melt strength (R ms ) of about 150 Pa·s 2 to about 10,000 Pa·s 2 , and the low melt strength polypropylene has a rheology melt strength (R ms ) of about 30 Pa·s 2 to about 90 Pa·s 2 .
3. The container of claim 1 , wherein the material comprises the blend of the high melt strength polypropylene and the low melt strength polypropylene, and the material comprises from about 40 to about 90 percent by weight of the high melt strength polypropylene and from about 10 to about 60 percent by weight of the low melt strength polypropylene.
4. The container of claim 1 , wherein the material comprises the blend of the high melt strength polypropylene and the low melt strength polypropylene, and the material comprises from about 30 to about 80 percent by weight of the high melt strength polypropylene and from about 20 to about 70 percent by weight of the low melt strength polypropylene.
5. The container of claim 1 , wherein the material comprises the blend of the high melt strength polypropylene and the low melt strength polypropylene, and the material has a rheology melt strength (R ms ) of at least 130 Pa·s 2 .
6. The container of claim 1 , wherein the material comprises the blend of the high melt strength polypropylene and the low melt strength polypropylene, and the material has a rheology melt strength (R ms ) from about 130 Pa·s 2 to about 1,000 Pa·s 2 .
7. The container of claim 1 , wherein the material comprises the blend of the low melt strength polypropylene and the high density polyethylene, and the low melt strength polypropylene has a rheology melt strength (R ms ) of at least 10 Pa·s 2 .
8. The container of claim 1 , wherein the material comprises the blend of the low melt strength polypropylene and the high density polyethylene, and the material comprises from about 10 to about 90 percent by weight of the low melt strength polypropylene and from about 10 to about 90 percent by weight of the high density polyethylene.
9. The container of claim 1 , wherein the material comprises the blend of the low melt strength polypropylene and the high density polyethylene, and the material comprises from about 30 to about 80 percent by weight of the low melt strength polypropylene and from about 20 to about 70 percent by weight of the high density polyethylene.
10. The container of claim 1 , wherein the material comprises a blend of a high melt strength polypropylene and a high density polyethylene, and the material comprises from about 10 to about 90 percent by weight of the high melt strength polypropylene and from about 10 to about 90 percent by weight of the high density polyethylene.
11. The container of claim 1 , wherein the material comprises a blend of a high melt strength polypropylene and a high density polyethylene, and the material comprises from about 30 to about 80 percent by weight of the high melt strength polypropylene and from about 20 to about 70 percent by weight of the high density polyethylene.
12. The container of claim 1 , wherein the container wall has a thickness from about 0.1 mm to about 2.0 mm.