R-T-B-based alloy powder and method for producing same, and R-T-B-based sintered magnet and method for producing same
View Patent ↗A method is provided for producing an R-T-B based alloy powder. The method includes providing an alloy powder containing 27.5 to 36.0 mass % of R, where R is at least one among the rare-earth elements and always includes at least one of Nd and Pr, 0.85 to 1.05 mass % of B, 0.1 to 2.5 mass % of element M (Al, Ti, V, Cr, Mn, Ni, Cu, Zn, Ga, Zr, Nb, Mo, Ag, In, Sn, Hf, Ta, W, Pb and/or Bi), and a balance T, where T is Fe or is Fe and Co; and pulverizing the powder by introducing the powder and a pulverization gas in a pulverization chamber. The pulverization includes attrition while circulating the alloy powder with a flow of the pulverization gas in the pulverization chamber. The pulverization gas has a gauge pressure of 0.75 MPa or more, and the residence time is 6 minutes or more.
1. A production method of an R-T-B based alloy powder comprising:
a step of providing an alloy powder containing not less than 27.5 mass % and not more than 36.0 mass % of R (where R is at least one among the rare-earth elements and always includes at least one of Nd and Pr), not less than 0.85 mass % and not more than 1.05 mass % of B (boron), not less than 0.1 mass % and not more than 2.5 mass % of element M (where M is at least one selected from the group consisting of Al, Ti, V, Cr, Mn, Ni, Cu, Zn, Ga, Zr, Nb, Mo, Ag, In, Sn, Hf, Ta, W, Pb and Bi), and a balance T (where T is: Fe; or Fe and Co); and
a step of pulverizing the alloy powder by introducing the alloy powder and a pulverization gas in a pulverization chamber of a jet mill, wherein the pulverization comprises attrition while circulating the alloy powder with a flow of the pulverization gas in the pulverization chamber,
the pulverizing step being performed so as to satisfy the condition that the pulverization gas to be introduced in the pulverization chamber has a gauge pressure of 0.75 MPa or more and that a residence time of the alloy powder in the pulverization chamber is 6 minutes or more.
2. A production method of a sintered R-T-B based magnet comprising:
a step of obtaining an R-T-B based alloy powder by the method of claim 1 ; and
a step of aligning the R-T-B based alloy powder with an external magnetic field and sintering the R-T-B based alloy powder.
3. The production method of claim 1 , wherein the pulverizing step produces the R-T-B based alloy powder, in which 20% or more by number ratio of particles of the R-T-B based alloy powder satisfies the condition L/d≤5.39-1.07(a/b), given a ratio a/b between a longer diameter a that represents a largest diameter of each contour shape and a shorter diameter b that represents a largest diameter of each contour shape in a direction orthogonal to the longer diameter a and given a ratio L/d between a circumferential length L and an equivalent circular diameter d, which is a diameter of a circle of an identical area, of contour shapes resulting from two-dimensional projection of the particles.