High residual content (HRC) kraft/soda lignin as an ingredient in wood adhesives
Most processes currently being proposed and/or used for the production of lignin from kraft or soda black liquors are capable of producing two main types of lignin: high residual content (HRC) lignin and low residual content (LRC) lignin. Surprisingly, it was discovered that HRC lignin, is a suitable ingredient in alkaline adhesives, particularly wood adhesives of the phenolic type (e.g. resole resins). This biomaterial is environmentally green and remarkably low cost, which makes it an industrially viable material to be used as a novel and major ingredient in phenolic adhesives for the manufacture of exterior grade plywood, laminated veneer lumber, oriented strand board (OSB) and other wood products—this was successfully demonstrated in a number of laboratory experiments as well as several different mill trials. The composition, preparation and application of such wood adhesives are hereby disclosed.
1. A wood adhesive comprising a residual content of lignin and
at least one of
i) a formaldehyde; a phenol; and a sodium hydroxide or ii) a phenol formaldehyde resin,
wherein the lignin has an ash content of greater than 19.53 to 30 wt % ash, and a pH of greater than 9.66 to 11.2.
2. The wood adhesive of claim 1 , wherein the lignin is selected from the group consisting of softwood, hardwood, annual plants and combinations.
3. The wood adhesive of claim 1 wherein the lignin is 0.5 to 50 wt % of the adhesive solids.
4. The wood adhesive of claim 3 wherein the lignin is 2.5 to 30 wt % of the adhesive solids.
5. A method of producing a wood adhesive comprising
providing a residual content of lignin, wherein the lignin has an ash content of greater than 19.53 to 30 wt % ash, and a pH of greater than 9.66 to 11.2; and
at least one of
i) providing a formaldehyde, a phenol and a sodium hydroxide; or ii) providing a phenol formaldehyde resin;
mixing the lignin and either i) the sodium hydroxide, formaldehyde and phenol or ii) the phenol formaldehyde resin to produce the adhesive.
6. The method of claim 5 wherein the lignin is 0.5 to 50 wt % of the adhesive.
7. The method of claim 6 , wherein the lignin is 2.5 to 30 wt % of the adhesive.
8. An adhesive comprising
a residual content of lignin, wherein the lignin has an ash content of greater than 19.53 to 30 wt % ash, and a pH of greater than 9.66 to 11.2, and
at least one of the following selected from the group consisting of i) a formaldehyde, a phenol, a sodium hydroxide; ii) a phenol formaldehyde resin; iii) Melamine-Urea-Phenol-Formaldehyde (MUPF) resin; iv) phenol resorcinol formaldehyde (PRF) resin; and combinations thereof.
9. The wood adhesive of claim 1 , wherein said lignin is a kraft lignin.
10. The method of claim 5 , wherein the lignin is directly produced from a kraft lignin recovery system.
11. The adhesive of claim 8 , wherein the lignin is directly produced from a kraft lignin recovery system.
12. The adhesive of claim 10 , wherein the kraft lignin recovery system is the LignoForce system.
13. The adhesive of claim 11 , wherein the kraft lignin recovery system is the LignoForce system.