Sodium-aluminum battery with sodium ion conductive ceramic separator
The present invention provides a sodium-aluminum secondary cell. The cell includes a sodium metal negative electrode, a positive electrode compartment that includes an aluminum positive electrode disposed in a positive electrolyte mixture of NaAl 2 X 7 and NaAlX 4 , where X is a halogen atom or mixture of different halogen atoms selected from chlorine, bromine, and iodine, and a sodium ion conductive electrolyte membrane that separates the negative electrode from the positive electrolyte. In such cases, the electrolyte membrane can include any suitable material, including, without limitation, a NaSICON-type membrane. Generally, when the cell functions, both the sodium negative electrode and the positive electrolyte are molten and in contact with the electrolyte membrane. Additionally, the cell is functional at an operating temperature between about 100° C. and about 200° C.
1. A sodium-aluminum secondary cell, comprising:
a metal sodium negative electrode, which electrochemically oxidizes to release sodium ions during discharge and electrochemically reduces sodium ions to sodium metal during recharging;
a positive electrode compartment comprising an aluminum positive electrode disposed in a positive electrolyte comprising a mixture of NaAl 2 X 7 and NaAlX 4 ,
wherein:
X is a halogen atom or mixture of different halogen atoms selected from chlorine, bromine, and iodine; and
the NaAl 2 X 7 , NaAlX 4 , or both NaAl 2 X 7 and NaAlX 4 are reduced to form aluminum during discharge; and
a sodium ion conductive electrolyte membrane that comprises a NaSICON-type material and separates the metal sodium negative electrode from the positive electrolyte,
wherein the metal sodium negative electrode and the positive electrolyte are molten and in contact with the conductive electrolyte membrane as the cell operates, and wherein the cell functions at an operating temperature between about 100° C. and about 200° C.
2. The cell of claim 1 , wherein the NaSICON-type material comprises a composite membrane having a porous layer and a dense functional layer.
3. The cell of claim 1 , wherein the cell functions when the operating temperature is between about 100° C. and about 150° C.
4. The cell of claim 1 , wherein the following reaction occurs at the positive electrode as the cell is discharged: NaAl 2 Cl 7 +3Na + +3e − →Al+3NaCl+NaAlCl 4 .
5. The cell of claim 1 , wherein the following reaction occurs at the positive electrode as the cell is discharged: NaAlCl 4 +3Na + +3e − →Al+4NaCl.
6. The cell of claim 1 , wherein the one or both of the following reactions occurs at the positive electrode as the cell is discharged: NaAl 2 Cl 6 I+3Na + +3e − →Al+3NaCl+NaAlCl 3 I, NaAlCl 6 I+3Na + +3e − →Al+NaI+2NaCl+NaAlCl 4 .
7. The cell of claim 1 , wherein the following reaction occurs at the positive electrode as the cell is discharged: NaAlCl 3 I+3Na + +3e − →Al+3NaCl+NaI.
8. The cell of claim 1 , wherein the positive electrolyte comprises NaAlCl 3 I.
9. The cell of claim 1 , wherein the positive electrolyte comprises NaAl 2 Cl 6 I.
10. A method for providing electrical potential from a sodium-aluminum secondary cell, the method comprising:
providing a molten sodium secondary cell, comprising:
a metal sodium negative electrode, which electrochemically oxidizes to release sodium ions during discharge and electrochemically reduces sodium ions to sodium metal during recharging;
a positive electrode system comprising an aluminum positive electrode disposed in a positive electrolyte comprising a mixture of NaAl 2 X 7 and NaAlX 4 , where X is a halogen atom or mixture of different halogen atoms selected from chlorine, bromine, and iodine; and
a sodium ion conductive electrolyte membrane that comprises a NaSICON-type material and separates the metal sodium negative electrode from the positive electrolyte; and
heating the metal sodium negative electrode to a temperature between about 100° C. and about 200° C. so that the metal sodium negative electrode is molten and in contact with the sodium ion conductive electrolyte membrane and so that the positive electrolyte is molten and in contact with the sodium ion conductive electrolyte membrane, such that the metal sodium negative electrode oxidizes to release the sodium ions and such that the NaAl 2 X 7 , NaAlX 4 , or both NaAl 2 X 7 and NaAlX 4 are reduced to form aluminum, thereby allowing the cell to discharge electricity.
11. The method of claim 10 , further comprising maintaining the temperature of the metal sodium negative electrode between about 110° C. and about 130° C.
12. The method of claim 10 , further comprising maintaining the temperature of the positive electrolyte at an operating temperature between about 110° C. and about 180° C.
13. The method of claim 10 , further comprising maintaining the temperature of the positive electrolyte at an operating temperature between about 110° C. and about 150° C.
14. The method of claim 10 , further comprising recharging the cell by passing an electrical potential between the sodium metal negative electrode and the positive electrode to cause the sodium negative electrode to electrochemically reduce sodium ions to sodium metal.
15. The method of claim 1 , wherein the one or both of the following reactions occurs at the positive electrode as the cell is discharged: NaAl 2 Cl 6 I+3Na + +3e − →Al+3NaCl+NaAlCl 3 I, NaAl 2 Cl 6 I+3Na + +3e − →Al+NaI+2NaCl+NaAlCl 4 .
16. The method of claim 1 , wherein the following reaction occurs at the positive electrode as the cell is discharged: NaAlCl 3+3 Na + +3e − →Al+3NaCl+NaI.
17. The method of claim 1 , wherein the positive electrolyte comprises NaAlCl 3 I.
18. The method of claim 1 , wherein the positive electrolyte comprises NaAl 2 Cl 6 I.