Opaque adhesives in wet condition for label application
Various opacifying adhesive compositions are described. The adhesives exhibit relatively high levels of opacity in wet conditions while maintaining acceptable adhesive properties. Also described are label assemblies and labeled containers using such adhesives. Related methods of use and preparation are also described.
1. A label adapted to remain opaque in wet condition, said label comprising:
an outer layer of facestock for receiving printed indicia;
at least one opacifying adhesive layer underlying said facestock,
wherein said opacifying adhesive layer comprises an adhesive component and a pigment component in proportion sufficient to maintain opacity when exposed to an aqueous environment and a peel adhesion of at least 1 N/inch and a loop tack of at least 2 N/inch of the opacifying adhesive layer in a pressure sensitive application, and
wherein said pigment component comprises surface coated TiO 2 and wherein said pigment component is present in a weight range of about 10% to about 50% of said adhesive component; and
a liner, underlying said opacifying adhesive layer.
2. The label of claim 1 , wherein said adhesive component is a pressure sensitive adhesive.
3. The label of claim 1 , wherein said adhesive component is selected from the group consisting of emulsion adhesives, hot-melt adhesives, solvent adhesives, and combinations thereof.
4. The label of claim 1 , wherein said pigment component has a wet opacity greater than 70%.
5. The label of claim 1 , wherein said label further comprises a second adhesive layer underlying said opacifying adhesive layer.
6. The label of claim 5 , wherein said second adhesive layer is selected from the group consisting of emulsion adhesives, hot-melt adhesives, solvent adhesives, and combinations thereof.
7. The label of claim 5 , wherein the loop tack of the label is at least 3 newtons per inch (N/inch) when said facestock is paper, and when said pressure sensitive application is performed on a glass substrate.
8. The label of claim 5 , wherein the loop tack of the label is at least 2 newtons per inch (N/inch) when said facestock is paper, and when said pressure sensitive application is performed on a high density polyethylene (HDPE) substrate.
9. The label of claim 1 , wherein said adhesive component includes acrylic adhesive.
10. The label of claim 1 , wherein said opacity in wet condition is about 80% to 90%.
11. The label of claim 1 , wherein said pressure sensitive application is performed on a substrate comprising glass.
12. The label of claim 1 , wherein said pressure sensitive application is performed on a high density polyethylene (HDPE) substrate.
13. The label of claim 1 , wherein said facestock comprises a paper facestock.
14. The label of claim 1 , wherein said facestock comprises a plastic facestock.
15. The label of claim 1 , wherein said loop tack is at least 3 newtons per inch (N/inch) when said facestock is paper, and when said pressure sensitive application is performed on a glass substrate.
16. The label of claim 1 , wherein said loop tack is at least 2 newtons per inch (N/inch) when said facestock is paper, and when said pressure sensitive application is performed on a high density polyethylene (HDPE) substrate.
17. The label of claim 1 , wherein said opacifying adhesive layer has a coat weight of about 16 to about 30 grams per square meter (gsm).
18. The label of claim 1 , wherein said opacifying adhesive layer has a coat weight, of about 22 to about 26 grams per square meter (gsm).
19. The label of claim 1 further comprising:
a clear or transparent layer.
20. The label of claim 1 further comprising:
a metallic layer.