Separator having adhesive layer, manufacturing method of the same, and electrochemical device having the same

1. A heat-resistant separator comprising a porous film, a polymeric fibrous web situated in a face to face relationship with the porous film, and an adhesive binder layer located between the porous film and the fibrous layer, said binder layer comprising an adhesive and covering at least a portion of the surface of the porous film that faces the fibrous web, wherein;

the fibrous layer comprises fibers having diameters in the range of 1-3000 nm and a mean fiber diameter in the range of 1-3000 nm, a majority of said fibers manufactured of a polyimide,

the amount of adhesive present between the porous film and the fibrous web in the final product is within the range of 0.30 grams per square meter of covered surface of porous film to 0.90 grams per square meter of covered surface of porous film,

the mean flow pore size of the fibrous layer is 1.5 μm or greater.

2. The separator of claim 1 in which the amount of adhesive present between the porous film and the fibrous web in the final product is within the range of 0.40 grams per square meter of covered surface of porous film to 0.90 grams per square meter of covered surface of porous film.

3. The separator of claim 1 wherein the adhesive is selected from the group consisting of polyvinylidene fluoride, polyvinylidene fluoride-co-hexafluoropropylene, polymethyl methacrylate, polyacrylonitrile, polyvinylpyrrolidone, polyvinyl acetate, polyethylene oxide, cellulose acetate, polyvinyl alcohol, carboxymethyl cellulose, sodium carboxymethyl cellulose, a meta-aramid, a para-aramid, styrene butadiene rubber, and mixtures thereof.

4. A process for preparing a heat-resistant separator comprising the steps of

(i) providing a porous film and a polymeric fibrous web,

(ii) coating an adhesive solution layer comprising an adhesive and a solvent onto a surface of the porous film, and covering at least a portion of the surface of the porous film,

(iii) placing the web onto the surface of the porous film that contains the adhesive solution to form a film plus fibrous web laminate with an adhesive solution located in between the faces of the film and the fibrous web,

(iv) applying sufficient heat to the laminate to remove the solvent, wherein;

the fibrous web comprises fibers having diameters in the range of 1-3000 nm, a majority of said fibers manufactured of a polyimide,

the porosity of the fibrous web prior to step (iii) is greater than or equal to 65%,

the mean flow pore size of the fibrous web prior to step (iii) is 1.5 microns or greater,

the Frazier air permeability of the fibrous web prior to step (iii) is 2.0 cfm/ft 2 or greater,

the coating thickness ratio of the adhesive solution layer prior to step (iv) is greater than or equal to 1.0 and less than or equal to 2.0, and

the adhesive solution layer comprises the adhesive at a concentration of 1 percent or greater by weight of adhesive solution, a C3 or higher alcohol that is not isopropanol and a remainder of deionized water such that the contact angle of the adhesive solution with respect to the microporous membrane is within the range of 50°-90°.

5. The process of claim 4 wherein the adhesive is selected from the group consisting of polyvinylidene fluoride, polyvinylidene fluoride-co-hexafluoropropylene, polymethyl methacrylate, polyacrylonitrile, polyvinylpyrrolidone, polyvinyl acetate, polyethylene oxide, cellulose acetate, polyvinyl alcohol, carboxymethyl cellulose, a meta-aramid, a para-aramid, styrene butadiene rubber, and mixtures thereof.

6. A heat-resistant separator made by the process of claim 4 in which the adhesive is sodium carboxymethylcellulose.

7. An electrochemical device comprising a cathode, an anode and a separator interposed between the cathode and the anode, wherein the separator is the separator of claim 1 .

8. The electrochemical device according to claim 7 , wherein the electrochemical device is a lithium secondary battery.