Reduction in stress cracking of films
Methods and packages for storing film strips while reducing or eliminating stress cracking during storage, including use of packages having an inner surface made from polymeric materials exhibiting various physical properties and including films and pouches that are annealed.
1. A method of packaging a pharmaceutical active-containing film strip comprising the steps of:
(a) forming a pharmaceutical active-containing film strip;
(b) providing a package, said package comprising:
(i) a top layer having an inner surface and an outer surface; and
(ii) a bottom layer having an inner surface and an outer surface, said inner surface of said bottom layer comprising at least one polymeric material having at least one physical characteristic selected from the group consisting of:
(1) a surface energy of about 100 degrees or greater, as measured by a water contact angle test; and
(2) a surface adhesivity level of less than about 0.25 lbf as measured by a peel force test using a load frame and packaging tape;
wherein said inner surface of said bottom layer has a surface RMS roughness of less than about 800 nm as measured by atomic force microscopy at a 100 micron square sample size level;
wherein said top layer and said bottom layer form a pocket therebetween when placed on top of each other;
(c) placing said film strip within said pocket; and
(d) sealing said top layer to said bottom layer so as to provide a sealed pocket.
2. The method of claim 1 , wherein said inner surface of said top layer comprises at least one polymeric material having at least one physical characteristic selected from the group consisting of:
(i) a surface energy of about 100 degrees or greater, as measured by a water contact angle test;
(ii) a surface adhesivity level of less than about 0.25 lbf as measured by a peel force test using a load frame and packaging tape; and
(iii) a surface RMS roughness of less than about 800 nm as measured by atomic force microscopy at a 100 micron square sample size level.
3. The method of claim 1 , wherein said film strip comprises polyethylene oxide.
4. The method of claim 3 , wherein said film strip further comprises a second polymeric material different from polyethylene oxide.
5. The method of claim 1 , wherein said surface adhesivity level of said inner surface of said bottom layer is less than about 0.20 lbf as measured by a peel force test using a load frame and packaging tape.
6. The method of claim 1 , wherein said surface RMS roughness of said inner surface of said bottom layer is less than about 700 nm as measured by atomic force microscopy at a 100 micron square sample size level.
7. The method of claim 2 , wherein said surface adhesivity level of said inner surface of said top layer is less than about 0.20 lbf as measured by a peel force test using a load frame and packaging tape.
8. The method of claim 2 , wherein said surface RMS roughness of said inner surface of said top layer is less than about 700 nm as measured by atomic force microscopy at a 100 micron square sample size level.
9. The method of claim 1 , wherein less than 5% of film strips stored in said package exhibit stress cracking after storage of three months at about room temperature.
10. A method of packaging a pharmaceutical active-containing film strip comprising the steps of:
(a) forming a pharmaceutical active-containing film strip;
(b) providing a package, said package comprising:
(i) a top layer having an inner surface and an outer surface; and
(ii) a bottom layer having an inner surface and an outer surface, said inner surface of said bottom layer comprising at least one polymeric material having at least two physical characteristics selected from the group consisting of:
(1) a surface energy of about 100 degrees or greater, as measured by a water contact angle test;
(2) a surface adhesivity level of less than about 0.25 lbf as measured by a peel force test using a load frame and packaging tape; and
(3) a surface RMS roughness of less than about 800 nm as measured by atomic force microscopy at a 100 micron square sample size level;
wherein said inner surface of said top layer comprises at least one polymeric material having at least one physical characteristic selected from the group consisting of:
(1) a surface energy of about 100 degrees or greater, as measured by a water contact angle test; and
(2) a surface adhesivity level of less than about 0.25 lbf as measured by a peel force test using a load frame and packaging tape;
wherein said inner surface of said top layer has a surface RMS roughness of less than about 800 nm as measured by atomic force microscopy at a 100 micron square sample size level; and
wherein said top layer and said bottom layer form a pocket therebetween when placed on top of each other;
(c) placing said film strip within said pocket; and
(d) sealing said top layer to said bottom layer so as to provide a sealed pocket.
11. A method of packaging a pharmaceutical active-containing film strip comprising the steps of:
(a) forming a pharmaceutical active-containing film strip;
(b) providing a package, said package comprising:
(i) a top layer having an inner surface and an outer surface; and
(ii) a bottom layer having an inner surface and an outer surface, said inner surface of said bottom layer comprising at least one polymeric material having at least two physical characteristics selected from the group consisting of:
(1) a surface energy of about 100 degrees or greater, as measured by a water contact angle test;
(2) a surface adhesivity level of less than about 0.25 lbf as measured by a peel force test using a load frame and packaging tape; and
(3) a surface RMS roughness of less than about 800 nm as measured by atomic force microscopy at a 100 micron square sample size level;
wherein said inner surface of said bottom layer comprises low density polyethylene;
(c) placing said film strip within said pocket; and
(d) sealing said top layer to said bottom layer so as to provide a sealed pocket.
12. A method of packaging a pharmaceutical active-containing film strip comprising the steps of:
(a) forming a pharmaceutical active-containing film strip;
(b) providing a package, said package comprising:
(i) a top layer having an inner surface and an outer surface; and
(ii) a bottom layer having an inner surface and an outer surface, said inner surface of said bottom layer comprising at least one polymeric material having at least two physical characteristics selected from the group consisting of:
(1) a surface energy of about 100 degrees or greater, as measured by a water contact angle test;
(2) a surface adhesivity level of less than about 0.25 lbf as measured by a peel force test using a load frame and packaging tape; and
(3) a surface RMS roughness of less than about 800 nm as measured by atomic force microscopy at a 100 micron square sample size level;
wherein said inner surface of said top layer comprises low density polyethylene;
(c) placing said film strip within said pocket; and
(d) sealing said top layer to said bottom layer so as to provide a sealed pocket.
13. The method of claim 10 , wherein said inner surface of said top layer has a surface RMS roughness of less than about 700 nm as measured by atomic force microscopy at a 100 micron square sample size level.
14. The method of claim 1 , wherein said pocket is hermetically sealed.
15. The method of claim 10 , wherein said pocket is hermetically sealed.
16. The method of claim 11 , wherein said pocket is hermetically sealed.
17. The method of claim 12 , wherein said pocket is hermetically sealed.