Diesel particulate filter
A method of making a filter for filtering particulate matter from exhaust gas emitted from a lean-burn internal combustion engine, which filter comprising a porous substrate having inlet surfaces and outlet surfaces, wherein the inlet surfaces are separated from the outlet surfaces by a porous structure containing pores of a first mean pore size, wherein the inlet surfaces comprise a bridge network comprising interconnected particles of refractory material over the pores of the porous structure, which method comprising the step of contacting inlet surfaces of the filter substrate with an aerosol comprising refractory material in dry powder form. The invention also relates to a filter obtainable by such method.
1. A method for producing a filter comprising spraying a dry particulate aerosol onto an inlet surface of a porous filter for filtering particulate matter from a lean-burn exhaust gas, to form a filter cake having a density of 0.3 to 1.2 g/in 3 , wherein said aerosol comprises inorganic particles selected from the group consisting of silicate zeolite, aluminosilicate zeolite, metal-substituted aluminosilicate zeolite, non-zeolitic molecular sieve, and metal oxide, provided that said metal oxide particles have an average size of greater than 0.2 μm and less than 5 μm,
wherein the filter comprises: (a) a porous substrate having an inlet surface and an outlet surface, wherein the inlet surface and the outlet surface are separated by a porous structure; and (b) a catalytic filter cake in the form of a bridge network on the inlet surface, said bridge network comprising interconnected inorganic particles selected from the group consisting of silicate zeolite, aluminosilicate zeolite, metal-substituted aluminosilicate zeolite, non-zeolitic molecular sieve, and metal oxide, provided that said metal oxide particles have an average size of greater than 0.2 μm and less than 5 μm, where the interconnected inorganic particles are dry aerosol deposited, the particles form a bridge over the pores.
2. The method of claim 1 wherein said inorganic particles of said aerosol are derived from a powder having a bulk density of 0.1 to 0.4 g/cm 3 .
3. The method of claim 1 wherein said dry particulate aerosol is deposited on an untreated substrate.
4. The method according to claim 1 , wherein the cake is derived from a powder having a bulk density of 0.05 to 1 g/cm 3 .
5. The method according to claim 1 , wherein the porous substrate as a mean pore diameter of about 11-22 μm.
6. The method according to claim 1 , wherein the porous substrate is a wall-flow filter.
7. The method according to claim 1 , wherein the cake is present in an amount less than 1.2 g/in 3 .
8. The method according to claim 1 , wherein the inorganic particles are a Selective Catalytic Reduction (SCR) catalyst.
9. The method according to claim 1 , wherein the inorganic particles are selected from the group consisting of alumina, silica, zirconia, ceria, chromia, magnesia, calcia, titania and mixed oxides of any two or more thereof.
10. The method of according claim 1 , wherein the inorganic particles are zeolite or a non-zeolite molecular sieve having a CHA framework.
11. The method according to claim 1 further comprising a catalytic washcoat selected from the group consisting of Three-Way-Catalyst (TWC), NOx absorber, oxidation catalyst, hydrocarbon trap, lean NOx catalyst, and combinations thereof.
12. The method according to claim 1 , wherein the inorganic particles do not substantially enter the pores of the porous substrate.