Method of making a hydroprocessing catalyst with a single step metal and chelant incorporation, the catalyst, and the use of the catalyst
A hydroprocessing catalyst composition that comprises a metal-incorporated support having incorporated therein a metal component and a chelating agent, and, further comprising a polar additive. The catalyst composition is prepared by incorporating in a single step at least one metal component and a chelating agent into a support material to form a metal-incorporated support followed by drying the metal-incorporated support and thereafter incorporating therein a polar additive.
1. A hydroprocessing catalyst composition, comprising:
a dried metal-incorporated support, and
an incorporated polar additive;
wherein said dried metal-incorporated support comprises a dried and calcined shaped support particle, having incorporated therein a metal component and a chelating agent selected from the group of compounds consisting of aminocarboxylic acids, polyamines, aminoalcohols, oximes, and polyethyleneimines, which has been dried thereby providing said dried metal-incorporated support;
wherein said incorporated polar additive is selected from the group of amide compounds having a polarity and a dipole moment of at least 0.45, and
wherein at least 75% of the available pore volume of said dried metal-incorporated support is filled with said polar additive.
2. A hydroprocessing catalyst composition as recited in claim 1 , wherein said hydroprocessing catalyst composition comprises a Group 9 or Group 10 metal component selected from the group consisting of cobalt and nickel present in an amount in the range of from 0.5 wt. % to 20 wt. %, and a Group 6 metal component selected from the group consisting of molybdenum and tungsten present in an amount in the range of from 5 wt. % to 50 wt. %, wherein the weight percents are based on the weight of the dry support material with the metal component as the element regardless of its actual form.
3. A hydroprocessing catalyst composition as recited in claim 2 , wherein said calcined shaped support particles comprise a porous refractory oxide selected from the group of refractory oxides consisting of silica, alumina, titania, zirconia, silica-alumina, silica-titania, silica-zirconia, titania-alumina, zirconia-alumina, silica-titania and combinations of two or more thereof; and wherein said calcined shaped support particles have a surface area (as determined by the BET method) in the range of from 50 m 2 /g to 450 m 2 /g, a mean pore diameter in the range of from 50 to 200 angstroms (Å), and a total pore volume exceeding 0.55 cc/g.
4. A hydroprocessing process, comprising: contacting under hydroprocessing reaction conditions the composition of claim 3 with a hydrocarbon feedstock.
5. A hydroprocessing process, comprising: contacting under hydroprocessing reaction conditions the composition of claim 2 with a hydrocarbon feedstock.
6. A hydroprocessing process, comprising: contacting under hydroprocessing reaction conditions the composition of claim 1 with a hydrocarbon feedstock.