Method for manufacturing electrical steel sheet
A treatment solution is applied on a surface of a base iron; and the treatment solution is baked and dried. The treatment solution contains a first component: 100 parts by mass in solid content, and a second component composed of particles of one or more kinds selected from a group consisting of a polyolefin wax, an epoxy resin and an acrylic resin, the particles having an average particle size of 2.0 μm to 15.0 μm and a melting point of 60° C. to 140° C.: 5 parts by mass to 45 parts by mass in resin solid content. The first component contains a colloidal silica: 100 parts by mass, and an emulsion of one kind selected from a group consisting of an acrylic resin, an epoxy resin and a polyester resin which have an average particle size of 0.05 μm to 0.50 μm, or an emulsion of a mixture or copolymer of two or three kinds selected from the group: 40 parts by mass to 400 parts by mass in resin solid content.
1. A method for manufacturing an electrical steel sheet, comprising: applying a treatment solution on a surface of a base iron: and
baking and drying the treatment solution,
wherein the treatment solution contains:
a first component: 100 parts by mass in solid content, the first component consisting of:
a colloidal silica having an average particle size of 5 nm to 40 nm and having an Na content of 0.5 mass % or less: 100 parts by mass; and
an emulsion of one kind selected from the group consisting of an acrylic resin, an epoxy resin and a polyester resin which have an average particle size of 0.05 um to 0.25 um, or an emulsion of a mixture or copolymer of two or three kinds selected from the group: 40 parts by mass to 400 parts by mass in resin solid content; and
a second component consisting of particles of one or more kinds selected from the group consisting of a polyolefin wax, an epoxy resin and an acrylic resin, the particles having an average particle size of 2.0 um to 15.0 um and a melting point of 60° C. to 140° C.: 5 parts by mass to 40 parts by mass in resin solid content,
wherein a solid content of the treatment solution substantially consists of the first component and the second component.
2. The method for manufacturing an electrical steel sheet according to claim 1 , wherein a temperature to be reached in the baking and drying is 150° C. to 300° C., and a time therefor is 3 seconds to 15 seconds.