Composite gypsum board and methods related thereto
Disclosed is a composite gypsum board comprising a board core and a concentrated layer of substantial thickness (e.g., at least about 0.02 inches). The concentrated layer includes a higher weight percentage of an enhancing additive than the board core. The board core has a thickness greater than the thickness of the concentrated layer and forms the bulk of the board volume. The concentrated layer has a higher density (e.g., at least about 1.1 times greater) than the density of the board core. Also disclosed is a method of preparing a composite gypsum board.
1. A method of making composite gypsum board, the method comprising:
(a) preparing a first slurry comprising stucco, water and enhancing additive;
(b) applying the first slurry in a bonding relation to a first cover sheet to form a concentrated layer, the concentrated layer having a first face and a second face, wherein the first concentrated layer face faces the first cover sheet;
(c) mixing at least water, stucco, and optionally the enhancing additive to form a second slurry;
(d) applying the second slurry in a bonding relation to the concentrated layer to form a board core having a first face and a second face, the first face of the board core facing the second face of the concentrated layer;
(e) applying a second cover sheet in bonding relation to the second board core face to form a board precursor; and
(f) drying the board precursor to form the composite gypsum board; wherein:
i. when the second slurry contains the enhancing additive, the enhancing additive is more concentrated in the first slurry than the second slurry,
ii. when dried, the board core has a dry thickness that is about 5 to about 35 times greater than the dry thickness of the concentrated layer,
iii. the board has a nail pull resistance according to ASTM C473-10, Method B of at least 68 lbs of force,
iv. the board has a dry density of about 33 pcf (about 530 kg/m 3 ) or less, and
v. the enhancing additive includes starch.
2. The method of claim 1 , wherein, when dried, the concentrated layer has a density of at least about 1.1 times higher than a density of the board core.
3. The method of claim 2 , wherein a density differential between the concentrated layer and the board core is at least about 8 pcf (about 130 kg/m 3 ).
4. The method of claim 1 , wherein the board has a nail pull resistance according to ASTM C473-10, Method B of at least about 77 lbs of force.
5. The method of claim 1 , wherein the first slurry is mixed in a first mixer and the second slurry is mixed in a second mixer.
6. The method of claim 1 , wherein the starch comprises a pregelatinized starch having a viscosity of from about 20 centipoise to about 700 centipoise when the viscosity is measured while the starch is subjected to conditions according to the VMA method.
7. The method of claim 1 , wherein, when dried, the concentrated layer has a thickness of from about 0.02 inches (about 0.05 cm) to about 0.09 inches (about 0.23 cm).
8. The method of claim 1 , wherein first slurry contains at least about 6 times the enhancing additive contained in the second slurry.
9. The method of claim 1 , wherein, when dried, the concentrated layer has an average core hardness that is at least about 1.5 times greater than the average core hardness of the board core.
10. The method of claim 1 , wherein the first slurry further comprises glass fiber.
11. The method of claim 1 , wherein the starch comprises a pregelatinized starch having a viscosity of from about 20 centipoise to about 700 centipoise when the viscosity is measured while the starch is subjected to conditions according to the VMA method.
12. The method of claim 1 , wherein the board core forms 90% or more of the bulk volume of the board.
13. The method of claim 1 , wherein the enhancing additive further includes one or more of polyvinyl alcohol, boric acid, gypsum-cement, nano-cellulose and micro-cellulose.
14. A method of making composite gypsum board, the method comprising:
(a) mixing at least water, stucco and enhancing additive to form a first slurry having a water-stucco ratio of from about 0.7 to about 2;
(b) applying the first slurry in a bonding relation to a first cover sheet to form a concentrated layer having a first face and a second face;
(c) mixing at least water, stucco, and optionally the enhancing additive to form a second slurry having a water-stucco ratio of from about 0.3 to about 1.1;
(d) applying the second slurry in a bonding relation to the concentrated layer to form a board core having a first density, the board core having a first face and a second face, wherein the first face of the board core faces the first face of the concentrated layer and the second face of the concentrated layer faces the first cover sheet;
(e) applying a second cover sheet in bonding relation to the second face of the board core to form the composite gypsum board: and
(f) drying the board; wherein:
i. when the second slurry contains the enhancing additive, the enhancing additive is more concentrated in the first slurry than the second slurry,
ii. when dried the board core has a dry thickness that is about 5 to about 35 times greater than the dry thickness of the concentrated layer, and
iii. the board has a hail pull resistance according to ASTM C473-10, Method B of at least about 68 lbs of force,
iv. the board has a dry density of about 33 pcf (about 530 kg/m 3 ) or less, and
v. the enhancing additive includes starch.
15. The method of claim 14 , wherein, when dried, the concentrated layer has a density of at least about 1.1 times higher than a density of the board core.
16. The method of claim 14 , wherein, when dried, the concentrated layer has a thickness of from about 0.02 inches (about 0.05 cm) to about 0.09 inches (about 0.23 cm).
17. The method of claim 14 , wherein the first slurry is mixed in a first mixer and the second slurry is mixed in a second mixer.
18. The method of claim 14 , wherein the second mixer has a higher mixing volume capacity than the first mixer.
19. The method of claim 14 , further comprising applying a bonding layer between the second cover sheet and the board core.
20. The method of claim 14 , wherein the board a nail pull resistance of at least about 77 lbs of force according to ASTM C473-10, Method B.
21. The method of claim 14 , wherein, when dried, the concentrated layer has an average core hardness that is at least about 1.5 times greater than the average core hardness of the board core.
22. The method of claim 14 , wherein the board core forms 90% or more of the bulk volume of the board.
23. The method of claim 14 , wherein the enhancing additive further includes one or more of polyvinyl alcohol, boric acid, gypsum-cement, nano-cellulose and micro-cellulose.