Method of producing a glueless dustless composite flooring material system

1. A method of producing a glueless dustless composite flooring material, comprising:

(i) forming a flooring base layer by:

(a) providing a PVC resin mixture free of compressed cellulose material and adhesive and having compatible materials, by mixing PVC resin and the compatible materials, yielding a PVC-resin mixture;

(b) fusing the PVC-resin mixture by application of heat and continued mixing;

(c) cooling the fused PVC-resin mixture;

(d) delivering the cooled fused PVC-resin mixture to another area for further processing;

(e) extruding the delivered cooled fused PVC-resin mixture at elevated temperature and pressure;

(f) mold forming the extruded PVC-resin mixture into a sheet of said flooring base layer; and

(g) cooling the sheet of said flooring base layer; and

(ii) forming a flooring face layer, by:

(a) providing a PVC decorative polymer film and a PVC wear-resistant polymer film;

(b) adding the PVC wear-resistant polymer film to the top face of said PVC decorative polymer film;

(c) hot-melt overlaying of said flooring face layer and said flooring base layer, yielding a sheet-form base-and-face subassembly;

(d) conditioning said sheet-form base-and-face subassembly;

(e) coating said sheet-form base-and-face subassembly with a UV-curing plastic resin, thereby forming a flooring coating layer;

(f) UV curing said coating of UV-curing plastic resin by exposure to UV light, yielding a finished-large-sheet assembly;

(g) profile processing said finished-large-sheet assembly, yielding multiple composite-flooring-material segments of desired size and shape, thereby producing a waterproof floor covering free of water-based materials;

(h) inspecting said composite-flooring-material segments; and

(i) packing said composite-flooring-material segments;

where forming of said flooring face layer and forming of said flooring base layer can be performed simultaneously, yielding a supply of both to said hot-melt overlaying process;

where said hot-melt overlaying process can accommodate an essentially constant supply of said flooring face layer and said flooring base layer, and produce an essentially constant supply of said sheet-form base-and-face subassembly;

where said conditioning process can be accomplished without slowing or stopping the pace of the essentially constant supply of said sheet-form base-and-face subassembly;

where said coating process can be accomplished at the pace of the essentially constant supply of said sheet-form base-and-face subassembly; and

where said UV curing process can be accomplished at the pace of the essentially constant supply of said sheet-form base-and-face subassembly.

2. The method of producing the glueless dustless composite flooring material of claim 1 , where said forming the flooring base layer further comprises forming a first extruded base sublayer and a second co-extruded base sublayer fused atop the first base sublayer, each sublayer being formed by mixing, fusing, cooling, delivering, and co-extruding, followed by common mold forming, the second co-extruded sublayer having a mixture comprising PVC resin and compatible materials adapted to provide additional desired qualities in said flooring base layer, in use.

3. The method of producing the glueless dustless composite flooring material of claim 1 , further comprising attaching an underlayment layer.

4. The method of producing the glueless dustless composite flooring material of claim 1 , where said PVC decorative polymer film further comprises a colored film.

5. The method of producing the glueless dustless composite flooring material of claim 1 , where said forming a flooring decorative layer further comprises printing of a design upon said PVC decorative polymer film before addition of said PVC wear-resistant polymer film.

6. The method of producing the glueless dustless composite flooring material of claim 1 , further comprising texturing the face surface of said sheet-form base-and-face assembly after said hot-melt overlaying and before completion of said conditioning.

7. The method of producing the glueless dustless composite flooring material of claim 1 , where said PVC wear-resistant polymer film is transparent.

8. The method of producing the glueless dustless composite flooring material of claim 1 , where said flooring coating layer is transparent.

9. The method of producing the glueless dustless composite flooring material of claim 1 , where said flooring coating layer further comprises a gritty particulate material.

10. The method of producing the glueless dustless composite flooring material of claim 1 , where said flooring coating layer further comprises aluminum oxide.

11. The method of producing the glueless dustless composite flooring material of claim 1 , where said PVC-resin mixture further comprises:

50 kg PVC;

75-100 kg 800-1000 mesh calcium carbonate (CaCO 3 );

3.8-5.0 kg Ca/Zn Heat Stabilizer;

2.5-4.0 kg Chlorinated polyethylene elastomer (CPE);

3.0-4.0 kg Acrylic (ACR) Modifier;

0.2-0.3 kg High density polyethylene oxide OA6;

0.4-0.6 kg Internal lubricant; and

0.5-0.7 kg High melting point polymer PE-wax.

12. The method of producing the glueless dustless composite flooring material of claim 1 , where said PVC-resin mixture further comprises:

50 kg PVC;

25-50 kg 800-1000 mesh calcium carbonate (CaCO 3 );

3.0-4.0 kg Ca/Zn Heat Stabilizer;

2.0-4.0 kg Chlorinated polyethylene elastomer (CPE);

2.0-3.5 kg Acrylic (ACR) Modifier;

0.1-0.2 kg High density polyethylene oxide OA6;

0.2-0.4 kg Internal lubricant;

0.15-0.35 kg High melting point polymer PE-wax; and

1.0-2.0 kg Epoxidized soybean oil.

13. The method of producing the glueless dustless composite flooring material of claim 1 , where said flooring coating layer further comprises an application of UV-curing primer and at least one application of UV-curing top coat.

14. The method of producing the glueless dustless composite flooring material of claim 1 , where said curing by exposure to UV light further comprises exposure to Mercury (Hg) lamps.

15. The method of producing the glueless dustless composite flooring material of claim 1 , where said curing by exposure to UV light further comprises exposure to Gallium (Ga) lamps.

16. The method of producing the glueless dustless composite flooring material of claim 1 , where formation of said flooring base layer further comprises heating the mixture to 115-130° C. while stirring at a high speed approaching but not exceeding 1600 RPM.

17. The method of producing the glueless dustless composite flooring material of claim 1 , where hot-melt overlaying of said flooring face layer and said flooring base layer further comprises passing the assembled flooring base layer and the flooring face layer through at least one set of heated rollers.

18. A method of producing a glueless dustless composite flooring material, comprising:

(i) forming a flooring base layer by:

(a) providing a PVC resin mixture having compatible materials, by mixing PVC resin and the compatible materials, yielding a PVC-resin mixture;

(b) fusing the PVC-resin mixture by application of heat and continued mixing,

(c) cooling the fused PVC-resin mixture;

(d) delivering the cooled fused PVC-resin mixture to another area for further processing;

(e) extruding the delivered cooled fused PVC-resin mixture at elevated temperature and pressure, where extrusion of said flooring base layer further comprises extrusion using an 80 mm-diameter screw at a speed not exceeding 40 RPM, an extrusion pressure of 20-35 mpa, and a temperature of 160-186° C.;

(f) mold forming the extruded PVC-resin mixture into a sheet of said flooring base layer; and

(g) cooling the sheet of said flooring base layer; and

(ii) forming a flooring face layer, by:

(a) providing a PVC decorative polymer film and a PVC wear-resistant polymer film;

(b) adding the PVC wear-resistant polymer film to the top face of said PVC decorative polymer film;

(c) hot-melt overlaying of said flooring face layer and said flooring base layer, yielding a sheet-form base-and-face subassembly;

(d) conditioning said sheet-form base-and-face subassembly;

(e) coating said sheet-form base-and-face subassembly with a UV-curing plastic resin, thereby forming a flooring coating layer;

(f) UV curing said coating of UV-curing plastic resin by exposure to UV light, yielding a finished-large-sheet assembly;

(g) profile processing said finished-large-sheet assembly, yielding multiple composite-flooring-material segments of desired size and shape, thereby producing a waterproof floor covering;

(h) inspecting said composite-flooring-material segments; and

(i) packing said composite-flooring-material segments;

where forming of said flooring face layer and forming of said flooring base layer can be performed simultaneously, yielding a supply of both to said hot-melt overlaying process;

where said hot-melt overlaying process can accommodate an essentially constant supply of said flooring face layer and said flooring base layer, and produce an essentially constant supply of said sheet-form base-and-face subassembly;

where said conditioning process can be accomplished without slowing or stopping the pace of the essentially constant supply of said sheet-form base-and-face subassembly;

where said coating process can be accomplished at the pace of the essentially constant supply of said sheet-form base-and-face subassembly; and

where said UV curing process can be accomplished at the pace of the essentially constant supply of said sheet-form base-and-face subassembly.

19. The method of producing the glueless dustless composite flooring material of claim 1 , where said PVC wear-resistant polymer film and said PVC decorative polymer film is supplied on large rolls.

20. A method of producing a glueless dustless composite flooring material, comprising:

(i) forming a flooring base layer comprising a PVC resin mixture free of compressed cellulose material and/or adhesive and having compatible materials, the flooring base layer being produced by:

(a) mixing a first PVC-resin mixture comprising, by weight:

(1) 36.93% polyvinylchloride;

(2) between 55.04% and 73.86% 800-1000 mesh calcium carbonate;

(3) between 2.81% and 3.69% calcium/zinc heat stabilizer;

(4) between 1.85% and 2.95% chlorinated polyethylene elastomer;

(5) between 2.22% and 2.95% acrylic modifier;

(6) between 0.15% and 0.22% polyethylene oxide;

(7) between 0.30% and 0.44% internal lubricant; and

(8) between 0.37% and 0.52% high melting point PE-wax;

(b) mixing a second PVC-resin mixture comprising, by weight:

(1) 59.92% polyvinylchloride;

(2) between 29.96% and 59.92% 800-1000 mesh calcium carbonate;

(3) between 3.59% and 4.79% calcium/zinc heat stabilizer;

(4) between 2.40% and 4.79% chlorinated polyethylene elastomer;

(5) between 2.40% and 4.19% acrylic modifier;

(6) between 0.12% and 0.24% polyethylene oxide;

(7) between 0.24% and 0.48% internal lubricant;

(8) between 0.18% and 0.42% high melting point PE-wax; and

(9) between 1.20% and 2.40% epoxidized soybean oil;

(c) separately fusing each PVC-resin mixture by application of heat and continued mixing;

(d) separately cooling the fused PVC-resin mixtures;

(e) separately delivering the cooled fused PVC-resin mixtures to another area for further processing;

(f) co-extruding the delivered cooled fused PVC-resin mixtures at elevated temperature and pressure;

(g) mold forming the co-extruded PVC-resin mixtures into a sheet of said flooring base layer; and

(h) cooling the sheet of said flooring base layer;

(ii) forming a flooring face layer, by:

(a) providing a PVC decorative polymer film;

(b) printing a decorative pattern upon the top face of said PVC decorative polymer film;

(c) adding a PVC wear-resistant polymer film to the top face of said PVC decorative polymer film;

(iii) hot-melt overlaying of said flooring face layer and said flooring base layer, yielding a sheet-form base-and-face subassembly;

(iv) conditioning said sheet-form base-and-face subassembly;

(v) coating said sheet-form base-and-face subassembly with a UV-curing plastic resin;

(vi) UV curing said coating of UV-curing plastic resin by exposure to UV light, yielding a finished-large-sheet assembly;

(vii) profile processing said finished-large-sheet assembly, yielding multiple composite-flooring-material segments of desired size and shape, thereby producing a waterproof floor covering free of water-based materials;

(viii) inspecting said composite-flooring-material segments; and

(ix) packing said composite-flooring-material segments;

where forming of said flooring face layer and forming of said flooring base layer can be performed simultaneously, yielding a supply of both to said hot-melt overlaying process;

where said hot-melt overlaying process can accommodate an essentially constant supply of said flooring face layer and said flooring base layer, and produce an essentially constant supply of said sheet-form base-and-face subassembly;

where said conditioning process can be accomplished without slowing or stopping the pace of the essentially constant supply of said sheet-form base-and-face subassembly;

where said coating process can be accomplished at the pace of the essentially constant supply of said sheet-form base-and-face subassembly; and

where said UV curing process can be accomplished at the pace of the essentially constant supply of said sheet-form base-and-face subassembly.