Cold applied asphalt coating composition and associated methods of use
The present description relates to asphalt coating compositions, and methods of application, for coating asphalt paving surfaces. In particular, sprayable coating compositions are provided, and methods of application, for coating asphalt paving surfaces. In the coating composition, a lightweight aggregate material of sprayable particle size is stably suspended in a sprayable asphalt emulsion in an amount sufficient to increase the micro-texture surface roughness of the cured coating.
1. A stable and sprayable asphalt composition comprising:
(a) from about 20% wt to about 55% wt of an asphalt binder composition, including:
(i) from about 3% wt to about 50% wt of a filler;
(ii) from about 1% wt to about 10% wt of a polymer;
(iii) from about 0.1% wt to about 4% wt of a rheology or viscosity modifier; and
(iv) from about 45% wt to about 55% wt of an asphalt emulsion;
(b) from about 45% wt to about 70% wt of aggregate; and
(c) the difference with water,
wherein the viscosity of the composition is from 2000 cp to about 8000 cp.
2. The asphalt binder composition of claim 1 , wherein at least one of:
the filler is clay;
the polymer is an acrylic polymer; or
a combination thereof.
3. The asphalt binder composition of claim 2 , wherein the clay is in an amount of from about 5% wt to about 25% wt.
4. The asphalt binder composition of claim 1 , further comprising a lightweight aggregate.
5. The asphalt binder composition of claim 4 , further comprising carbon black in an amount of from 1% wt to about 3% wt.
6. The asphalt binder composition of claim 1 , wherein the rheology or viscosity modifier is in an amount of from about 0.1% wt to about 3% wt.
7. The asphalt binder composition of claim 1 , further comprising a biocide in an amount of from 0.01% wt to about 0.3% wt.
8. The asphalt composition of claim 1 , wherein: the filler is present in an amount of about 5% wt to about 25% wt; and
the polymer is present in an amount of about 1% wt to about 10% wt.
9. The asphalt composition of claim 1 , wherein: the filler is present in an amount of about 5% wt to about 25% wt; and
the polymer is present in an amount of about 3% wt to about 8% wt.
10. The asphalt composition of claim 9 , wherein the polymer is acrylic polymer and the filler is clay.
11. A sprayable asphalt composition comprising from about 20% wt to about 55% wt of an asphalt binder composition, and from about 45% wt to about 70% wt of an aggregate based on the total weight of the sprayable asphalt composition, the difference with water, wherein the asphalt binder composition comprises:
from about 30% wt to about 60% wt of an asphalt or bitumen emulsion,
from about 3% wt to about 60% wt of a filler, and
from about 0.01% wt to about 20% wt of a polymer,
wherein the viscosity of the composition is from 2000 cp to about 8000 cp.
12. An asphalt concrete composition comprising:
a. from about 40% wt to about 45% wt of an asphalt binder composition based on the total weight of the asphalt concrete composition, wherein the asphalt binder composition includes:
i. from about 45% wt to about 55% wt of an asphalt emulsion based on the total weight of the asphalt binder composition;
ii. from about 3% wt to about 8% wt of an acrylic polymer based on the total weight of the asphalt binder composition;
iii. from about 1% wt to about 3% wt of a viscosity modifier based on the total weight of the asphalt binder composition;
iv. from about 5% wt to about 25 wt % of clay based on the total weight of the asphalt binder composition;
v. from about 1% wt to about 3% wt of carbon black based on the total weight of the asphalt binder composition;
vi. from about 0.01% wt to about 1% wt of a biocide based on the total weight of the asphalt binder composition, to 100% wt with water, wherein the asphalt binder composition has helical viscosity of from about 2000 cp to about 8000 cp; and
b. from about 50% wt to about 55% wt of a lightweight aggregate based on the total weight of the asphalt concrete composition; and
c. to 100% wt with water.
13. A structure comprising a coating or layer of the asphalt composition of claim 12 .
14. The asphalt concrete composition of claim 12 , wherein:
the asphalt emulsion is present in an amount of about 45% wt to about 55% wt;
the filler is present in an amount of about 5% wt to about 25% wt;
the polymer is present in an amount of about 1% wt to about 10% wt;
the viscosity modifier is present in an amount of about 1% wt to about 3% wt; and
the carbon black is present in an amount of about 1% wt to about 3% wt.
15. The asphalt concrete composition of claim 12 , wherein:
the asphalt emulsion is present in an amount of about 45% wt to about 55% wt;
the filler is present in an amount of about 5% wt to about 25% wt;
the polymer is present in an amount of about 3% wt to about 8% wt;
the viscosity modifier is present in an amount of about 1% wt to about 3% wt; and
the carbon black is present in an amount of about 1% wt to about 3% wt.