Pharmaceutical compositions with enhanced performance and improved processability
View Patent ↗The presently disclosed and claimed inventive concept(s) relates to a polymer for enhancing drug performance and improving processability. Specifically, the polymer comprises hydroxypropyl methyl cellulose acetate succinate (HPMC-AS). On the HPMC-AS, the percentage of total succinoyl degree of substitution is less than 12% at C6-OH position and greater than 53% at C3-OH, and the percentage of total acetyl degree of substitution is greater than 32% at C6-OH position.
1. A method for making hydroxypropyl methyl cellulose acetate succinate (HPMC-AS) comprising the steps of:
(a) reacting an amount of acetic anhydride and sodium acetate with a reaction mixture of hydroxyl propyl methylcellulose and acetic acid at a reaction temperature in a range from about 85 to about 115° C.;
(b) maintaining the reaction temperature for a time from about 30 minutes to about 2.0 hours to allow reaction and thereby form an intermediate having a percentage of a total degree of substitution (DS) of acetyl greater than 32% at a C6-OH position (% C6DSAc>32%) of the intermediate; and
(c) reacting the intermediate with an amount of succinic anhydride at the reaction temperature for a time from about 2.5 hours to about 23.5 hours to allow reaction and thereby form HPMC-AS having a percentage of a total DS of succinoyl less than 12% at a C6-OH position (% C6DSSuc<12%) and greater than 53% at a C3-OH position (% C3DSSuc>53%).
2. The method of claim 1 , wherein the HPMC-AS has a percentage of a total DS of acetyl less than 27% at a C3-OH position (% C3DSAc<27%).
3. The method of claim 1 , wherein the time in step (c) is varied from 2.5 hours to 15.5 hours.
4. The method of claim 3 , wherein the time in step (c) is varied from 2.5 hours to 5.5 hours.
5. The method of claim 1 , wherein the temperature is in a range from 95 to 115° C.
6. The method of claim 1 , wherein the temperature is in a range from 95 to 110° C.