Polyurethane foam-forming compositions, methods of making low density foams using such compositions, and foams formed therefrom
View Patent ↗Disclosed are polyurethane foam-forming compositions with a phase stable isocyanate-reactive composition that includes a halogenated olefin blowing agent that has low or no ozone depletion potential and low global warming potential. Such polyurethane foam-forming compositions are suitable for spray application to produce polyurethane foams that are believed to exhibit good fire resistance properties, low smoke generation and low or no scorch due to reduced exotherm, thereby making them particularly suitable for use, for example, as relatively thick wall and/or roof insulation.
1. A polyurethane foam-forming composition comprising:
(a) an isocyanate-reactive composition comprising:
(1) at least 50% by weight, based on the total weight of the isocyanate-reactive composition, of a phthalic anhydride based polyester polyol component;
(2) water; and
(3) a C 2 to C 6 halogenated olefin,
wherein the isocyanate-reactive composition exhibits no visible cloudiness or gels after aging the isocyanate-reactive composition for 7 days at 50° C.; and
(b) a polyisocyanate,
wherein the phthalic anhydride based polyester polyol component comprises a mixture of two or more phthalic anhydride based polyester polyols comprising:
(i) a first phthalic anhydride based polyester polyol having a hydroxyl number of 290 to 310 mg KOH/gram polyol and a OH functionality of 2.0 to 2.2, and
(ii) a second phthalic anhydride based polyester polyol having a hydroxyl number of 340 to 360 mg KOH/gram polyol and a OH functionality of 2.3 to 2.5.
2. The foam-forming composition of claim 1 , wherein:
(i) is present in an amount of 50% to 99% by weight, based on the combined weight of (i) and (ii); and
(ii) is present in an amount of 1% to 50% by weight, based on the combined weight of (i) and (ii).
3. The foam-forming composition of claim 1 , wherein the phthalic anhydride based polyester polyol component is present in an amount of at least 60% by weight, based on the total weight of the isocyanate-reactive composition.
4. The foam-forming composition of claim 1 , wherein the isocyanate-reactive composition further comprises a sucrose-based polyether polyol having a hydroxyl number of 400 to 800 mg KOH/gram polyol and an OH functionality of 5.0 to 7.0.
5. The foam-forming composition of claim 4 , wherein the sucrose-based polyether polyol is present in an amount of 1 to 20% by weight, based on the total weight of the isocyanate-reactive composition.
6. The foam-forming composition of claim 1 , wherein the C 2 to C 6 halogenated olefin comprises a hydrofluorochloroolefin.
7. The foam-forming composition of claim 6 , wherein the hydrofluorochloroolefin comprises 1,1,1-trifluoro-3-chloropropene (HFCO-1233zd).
8. A method of making a low density, polyurethane foam comprising:
(a) impingement mixing the foam-forming composition of claim 1 in a spray gun; and
(b) spraying the mixture onto a surface.
9. A polyurethane foam-forming composition comprising:
(a) an isocyanate-reactive composition comprising:
(1) at least 50% by weight, based on the total weight of the isocyanate-reactive composition, of a phthalic anhydride based polyester polyol component;
(2) water; and
(3) a C 2 to C 6 halogenated olefin; and
(b) a polyisocyanate,
wherein the phthalic anhydride based polyester polyol component comprises a mixture of two or more phthalic anhydride based polyester polyols comprising:
(i) a first phthalic anhydride based polyester polyol having a hydroxyl number of 290 to 310 mg KOH/gram polyol and a OH functionality of 2.0 to 2.2, and
(ii) a second phthalic anhydride based polyester polyol having a hydroxyl number of 340 to 360 mg KOH/gram polyol and a OH functionality of 2.3 to 2.5.
10. The foam-forming composition of claim 9 , wherein:
(i) is present in an amount of 50% to 99% by weight, based on the combined weight of (i) and (ii); and
(ii) is present in an amount of 1% to 50% by weight, based on the combined weight of (i) and (ii).
11. The foam-forming composition of claim 9 , wherein the phthalic anhydride based polyester polyol component is present in an amount of at least 60% by weight, based on the total weight of the isocyanate-reactive composition.
12. The foam-forming composition of claim 9 , wherein the isocyanate-reactive composition further comprises a sucrose-based polyether polyol having a hydroxyl number of 400 to 800 mg KOH/gram polyol and an OH functionality of 5.0 to 7.0.
13. The foam-forming composition of claim 12 , wherein the sucrose-based polyether polyol is present in an amount of 1 to 20% by weight, based on the total weight of the isocyanate-reactive composition.
14. The foam-forming composition of claim 9 , wherein the C 2 to C 6 halogenated olefin comprises a hydrofluorochloroolefin.
15. The foam-forming composition of claim 14 , wherein the hydrofluorochloroolefin comprises 1,1,1-trifluoro-3-chloropropene (HFC0-1233zd).
16. A method of making a low density, polyurethane foam comprising:
(a) impingement mixing the foam-forming composition of claim 9 in a spray gun; and
(b) spraying the mixture onto a surface.
17. Building wall or roof insulation comprising foam formed by the method of claim 16 .