Fire-rated roofing system
A fire-resistant polymeric membrane includes a polymer layer such as PVC, TPO, or EPDM affixed to a carbon fiber composite. The carbon fiber composite includes one or two layers of non-woven carbon fibers and at least one of an inert fiber mat or a metal foil layer, wherein the metal foil layer has a melting temperature of at least about 660° C. The present invention also provides an underlayment, wherein the underlayment is formed from one or more fibrous carbon layers affixed to at least one of an inert fiber mat or a metal foil having a melting temperature greater than 660° C.
1. A fire-resistant composite comprising:
a first layer comprising a flexible polyolefin sheet having a thickness of 45-80 mils, the first layer comprising a reinforcing material;
a second layer comprising first and second carbon fiber sheets with a metal foil positioned between said first and second carbon fiber sheets, the metal foil having a melting temperature above 660° C.; and
wherein said composite passes ASTM E 108 and is configured to be installed on a roof exterior.
2. The fire-resistant composite claimed in claim 1 wherein said first layer is affixed to said second layer to form a composite sheet.
3. The fire-resistant composite claimed in claim 1 wherein at least one of said carbon fiber sheets is tufted.
4. The fire-resistant composite claimed in claim 3 wherein said first and second carbon fiber sheets are affixed to said metal foil and to each other by tufting.
5. The fire-resistant composite claimed in claim 1 wherein said flexible polyolefin sheet is selected from the group consisting of thermoplastic polyolefin (TPO), ethylene propylene monomer rubber (EPM), ethylene propylene diene monomer rubber (EPDM).
6. The fire-resistant composite claimed in claim 1 wherein said metal foil is selected from the group consisting of aluminum, stainless steel, iron, iron alloys, titanium, nickel, chromium, tungsten, and copper.
7. The fire-resistant composite claimed in claim 6 wherein said metal foil has a melting temperature of at least about 1100° C.
8. The fire-resistant composite claimed in claim 7 wherein said metal foil has a melting temperature of at least 1200° C.
9. The fire-resistant composite claimed in claim 1 wherein the first carbon fiber sheet and the second carbon fiber sheet have a combined basis weight of at least 3 ounces per square yard.
10. The fire-resistant composite claimed in claim 1 wherein the first carbon fiber sheet and the second carbon fiber sheet have a combined basis weight of at least 6 ounces per square yard.
11. The fire-resistant composite claimed in claim 1 wherein the first carbon fiber sheet and the second carbon fiber sheet have a combined basis weight of at least 9 ounces per square yard.
12. The fire-resistant composite claimed in claim 1 wherein the first carbon fiber sheet and the second carbon fiber sheet have a combined basis weight of 9-12 ounces per square yard.
13. The fire-resistant composite claimed in claim 1 wherein said flexible polyolefin sheet comprises a first ply and a second ply and wherein said first ply includes the reinforcing material.