Low compression golf ball
A golf ball includes a core, a mantle and a cover layer. The core includes polybutadiene and has a diameter of less than 1.45 inches. The core has a deflection of at least 0.225 inches under an applied static load of 200 pounds. The mantle includes at least one fully neutralized ionomer terpolymer comprising ethylene, carboxylic acid and an acrylate. The mantle composition has a flexural modulus of less than 10,000 psi. The core and the mantle form a core-mantle assembly having a diameter of between 1.540 inches and 1.580 inches with a deflection of greater than 0.210 inches under an applied static load of 200 pounds. The cover layer includes one or more ionomer materials and has a Shore D hardness of greater than 62.
1. A golf ball comprising:
a core comprising polybutadiene and having a diameter of less than 1.45 inches, the core having a deflection of at least 0.220 inches under an applied static load of 200 pounds;
a mantle comprising a copolymer of ethylene and carboxylic acid, the mantle having a flexural modulus of less than 12,000 psi, wherein the core and the mantle form a mantle-core assembly having a diameter of between 1.52 inches and 1.6 inches with a deflection of greater than 0.210 inches under an applied static load of 200 pounds; and
a cover layer comprising one or more ionomer materials, the cover layer having a Shore D hardness of greater than 62.
2. The golf ball of claim 1 , wherein the polybutadiene has a cis-1,4 content of greater than 94%.
3. The golf ball of claim 1 , wherein the core additionally comprises a co-cross-linking agent and a free radical initiator.
4. The golf ball of claim 3 , wherein the co-cross-linking agent comprises a zinc salt of an unsaturated carboxylic acid.
5. The golf ball of claim 3 , wherein the free radical initiator comprises a peroxide.
6. The golf ball of claim 1 , wherein the core has a diameter of no greater than 1.40 inches.
7. The golf ball of claim 1 , wherein the core has a deflection of at least 0.225 inches under an applied static load of 200 pounds.
8. The golf ball of claim 1 , wherein the copolymer of the mantle comprises at least one ionomer, and wherein the at least one ionomer comprises a terpolymer of ethylene, a carboxylic acid and an acrylate.
9. The golf ball of claim 1 , wherein at least 30% of the carboxylic acid of the mantle is neutralized with metal ions.
10. The golf ball of claim 1 , wherein the carboxylic acid of the mantle is fully neutralized with metal ions.
11. The golf ball of claim 10 , wherein the copolymer comprises a fatty acid or metal salt of the copolymer.
12. The golf ball of claim 1 , wherein the copolymer comprises a terpolymer comprising 60 to 80% by weight ethylene, 8 to 20% by weight of α, β-unsaturated carboxylic acid and 5 to 25% by weight of n-alkyl acrylate.
13. The golf ball of claim 1 , wherein the mantle has a flexural modulus of less than 10,000 psi.
14. The golf ball of claim 1 , wherein the mantle-core assembly has a diameter of between 1.540 inches and 1.580 inches with a deflection of greater than 0.240 inches under an applied static load of 200 pounds.
15. The golf ball of claim 1 , wherein the golf ball has a compression of less than 20, wherein the compression is determined based upon the formula Compression=180 minus (deformation×1000).
16. A golf ball comprising:
a core comprising polybutadiene and having a diameter of no greater than 1.4 inches, the core having a deformation of at least 0.225 inches under an applied static load of 200 pounds;
a mantle comprising at least one fully neutralized ionomer comprising a terpolymer of ethylene, a carboxylic acid and an acrylate, the mantle having a flexural modulus of less than 10,000 psi, wherein the core and the mantle form a core-mantle assembly having a diameter of between 1.540 inches and 1.580 inches with a deformation of greater than 0.240 inches under an applied static load of 200 pounds; and
a cover layer comprising one or more ionomer materials, the cover layer having a Shore D hardness of greater than 62.
17. The golf ball of claim 16 , wherein the polybutadiene has a cis-1,4 content of greater than 94%.
18. The golf ball of claim 16 , wherein the golf ball has a compression of less than 20, wherein the compression is determined based upon the formula Compression=180 minus (deformation×1000).