An antimicrobial ceramic glazing composition contains one or more antimicrobial agents disposed therein. Methods for making and using the glazing composition are disclosed, as well as substrates having a fired antimicrobial glaze thereon. The antimicrobial agents comprise metallic oxides, with a subset of the disclosed combinations exhibiting synergistic effect in fired glazes.
1. A method for manufacturing a glazed ceramic substrate having an antimicrobial property, comprising:
applying an antimicrobial ceramic glazing composition to a substrate, the glazing composition including an antimicrobial composition comprising:
a first antimicrobial metal compound consisting of Bi 2 O 3 ,
a second antimicrobial metal compound consisting of ZnO, and
a third antimicrobial metal compound consisting of Ag 2 CO 3 ,
wherein the first antimicrobial metal compound is present in the glaze composition at a concentration of about one percent to about four percent, by weight of glaze composition; and
wherein the second antimicrobial metal compound is present in the glaze composition at a concentration of from about one percent to about four percent, by weight of glaze composition; and
wherein the third antimicrobial metal compound is present in the glaze composition at a concentration of from about 0.5 percent to about four percent, by weight of glaze composition; and
firing the glazing composition to transform the glazing composition into a fired glaze layer;
wherein the fired glazed layer possesses an antimicrobial property.
2. The method according to claim 1 wherein the first antimicrobial metal compound, the second antimicrobial metal compound and the third antimicrobial metal compound each have a concentration of about two percent in the antimicrobial ceramic glazing composition.
3. A glazed ceramic substrate having an antimicrobial property comprising:
a ceramic substrate having a first substrate surface; and
a fired antimicrobial composition disposed on the first substrate surface;
wherein the fired antimicrobial composition is a post-fired state of a ceramic glazing composition including:
a first antimicrobial metal compound consisting of Bi 2 O 3 ,
a second antimicrobial metal compound consisting of ZnO, and
a third antimicrobial metal compound consisting of Ag 2 CO 3 ,
wherein the first antimicrobial metal compound is present in the glaze composition at a concentration of about one percent to about four percent, by weight of glaze composition,
wherein the second antimicrobial metal compound is present in the glaze composition at a concentration of from about one percent to about four percent, by weight of glaze composition, and
wherein the third antimicrobial metal compound is present in the glaze composition at a concentration of from about 0.5 percent to about four percent, by weight of glaze composition.