Zn—Mg alloy-coated steel sheet with excellent blackening resistance and excellent adhesion
The present invention relates to a Zn—Mg alloy-coated steel sheet with excellent blackening resistance and excellent coating adhesion and to a method for manufacturing same. Provided are a Zn—Mg alloy-coated steel sheet with excellent blackening resistance and excellent adhesion and a method for manufacturing same, the steel sheet comprising: a substrate steel sheet; a Zn—Fe intermetallic compound layer formed on the substrate steel sheet; a first Zn—Mg coating layer formed on the Zn—Fe intermetallic compound layer and comprising a Zn—Fe intermetallic compound in which the content of Zn is 95% by weight or higher; a second Zn—Mg coating layer formed on the first Zn—Mg coating layer and comprising a Zn—Mg intermetallic compound in which the content of Zn is 80 to 95% by weight; and an oxide film formed on the second Zn—Mg coating layer and comprising a metallic oxide.
1. A Zn—Mg alloy-coated steel sheet having improved blackening resistance and coating adhesion, the Zn—Mg alloy-coated steel sheet comprising:
a base steel sheet;
a Zn—Fe intermetallic compound layer formed on the base steel sheet;
a first Zn—Mg coating layer formed on the Zn—Fe intermetallic compound layer and comprising a Zn—Mg intermetallic compound in which zinc (Zn) is included in an amount of 95 wt % or greater and less than 100 wt %;
a second Zn—Mg coating layer formed on the first Zn—Mg coating layer and comprising a Zn—Mg intermetallic compound in which zinc (Zn) is included in an amount of 80 wt % to 95 wt %; and
an oxide film formed on the second Zn—Mg coating layer, the oxide film being formed of SiO 2 film and having a thickness between 11 nm to 40 nm.
2. The Zn—Mg alloy-coated steel sheet of claim 1 , wherein the SiO 2 oxide film is formed by a combustion chemical vapor deposition (CCVD) process.
3. The Zn—Mg alloy-coated steel sheet of claim 2 , wherein in the CCVD process, an organic silane is used as a precursor.
4. The Zn—Mg alloy-coated steel sheet of claim 2 , wherein in the CCVD process, the base steel sheet is maintained within a temperature range of 330° C. to 450° C.
5. The Zn—Mg alloy-coated steel sheet of claim 1 , wherein the first Zn—Mg coating layer and the second Zn—Mg coating layer are formed using physical vapor deposition (PVD).