Fluoropolymers and membranes comprising fluoropolymers (III)
Disclosed are fluoropolymers with low CWST values and porous membranes made from the fluoropolymers. The fluoropolymer is made up of polymerized monomeric units of the formula A-X—CH 2 —B, wherein A is C 6 F 13 —(CH 2 ) 2 , X is O or S, and B is vinylphenyl, and the fluoropolymer has a weight average molecular weight (Mw) of at least 100 Kd and/or a glass transition temperature of at least 33° C. copolymer. The porous membranes are suitable for degassing a variety of fluids.
1. A porous membrane comprising a porous polymeric support and a fluoropolymer, wherein the fluoropolymer comprises polymerized monomeric units of the formula
A-X—CH 2 —B,
wherein A is C 6 F 13 —(CH 2 ) 2 , X is O or S, and B is vinylphenyl, and the fluoropolymer has a weight average molecular weight (Mw) of at least 100 Kd and/or a glass transition temperature of at least 33° C.,
wherein the porous polymeric support is selected from PVC/PAN, polysulfone, polyamide, cellulose, polyester, PPS, PPSU (polyphenyl sulfone), PVDF, PVF (polyvinyl fluoride), FEP (fluorinated ethylene-propylene), ETFE (polyethylenetetrafluoroethylene), PFPE (perfluoropolyether), PFSA (perfluorosulfonic acid), perfluoropolyoxetane, polyimide, polyether imide, polycarbonate, and polystyrene, and
wherein the porous membrane has a CWST of 15 to 23 dynes/cm.
2. The porous membrane of claim 1 , wherein B is meta-vinylphenyl, para-vinylphenyl, or a mixture thereof.
3. The porous membrane of claim 1 , wherein the monomeric unit is meta-[perfluorohexylethylenethiomethyl] styrene, para-[perfluorohexylethylenethiomethyl] styrene, or a mixture thereof.
4. The porous membrane of claim 1 , wherein the monomeric unit is meta-[perfluorohexylethyleneoxymethyl] styrene, para-[perfluorohexylethyleneoxymethyl] styrene, or a mixture thereof.
5. The porous membrane of claim 1 , wherein the fluoropolymer has a an Mw of at least 200 Kd.
6. The porous membrane of claim 1 , wherein the fluoropolymer has an Mw of 400 to 1300 Kd.
7. The porous membrane of claim 1 , wherein the fluoropolymer has an Mw of 1100 to 1300 Kd.
8. The porous membrane of claim 1 , wherein the porous polymeric support is selected from PVC/PAN, polysulfone, polyamide, cellulose, polyethersulfone, PPS, PPSU (polyphenyl sulfone), PFPE (perfluoropolyether), PFSA (perfluorosulfonic acid), perfluoropolyoxetane, polyimide, polyether imide, and polycarbonate.
9. A method of preparing a porous membrane according to claim 1 , the method comprising:
(i) dissolving the fluoropolymer in a solvent or mixture of solvents to obtain a solution comprising the fluoropolymer;
(ii) coating the solution from (i) on the porous polymeric support; and
(iii) evaporating the solvent or mixture of solvents from the coating to obtain the porous membrane.
10. The method of claim 9 , wherein the solvent or mixture of solvents comprises a halogenated solvent, optionally in combination with an alcohol.
11. The method of claim 10 , wherein the solvent or mixture of solvents is selected from methoxy nona-fluorobutane, methoxy nona-fluorobutane, chloroform, dichloromethane, 1,2-dichloroethane; 1,1,2-trichloro-1,2,2-trifluoroethane, 1,1,1,2,2-pentafluoro-3,3-dichloropropane, optionally in combination with isopropanol and/or 1,1,1,3,3,3-hexafluoro-2-propanol.
12. A method of filtering a fluid, the method comprising passing the fluid through the porous membrane of claim 1 .
13. The method of claim 12 , wherein a gas present in the fluid is removed from the fluid.