Bone treatment systems and methods
The present disclosure relates to bone cement formulations that have an extended working time for use in vertebroplasty procedures and other osteoplasty procedures together with cement injectors that include energy delivery systems for on-demand control of cement viscosity and flow parameters. The bone cement formulations may include a liquid component having at least one monomer and a non-liquid component including polymer particles and benzoyl peroxide (BPO). The non-liquid component may be further configured to allow controlled exposure of the BPO to the liquid monomer so as to enable control of the viscosity of the bone cement composition.
1. A bone cement system, comprising:
a pre-mixture comprising:
a first monomer-carrying component; and
a second polymer-carrying component, separate from the first monomer-carrying component, the second polymer-carrying component comprising a plurality of bead populations that have different mean particle sizes and an initiator in different amounts, the second polymer-carrying component comprising:
a first polymer bead population having a first mean particle size and including the initiator at a first weight percent of the first polymer bead population, wherein the initiator is integrated throughout the volume of the first polymer bead population; and
a second polymer bead population having a second mean particle size smaller than the first mean particle size and including the initiator at a second weight percent of the second polymer bead population, wherein the initiator is integrated throughout the volume of the second polymer bead population;
wherein upon forming a mixture of the first monomer-carrying component and the second polymer-carrying component, and after an initial exposure period post-mixing, the mixture is characterized as having a time-viscosity curve slope that remains less than or equal to about 200 Pa·s/minute until the mixture reaches a viscosity of about 3000 Pa·s.
2. The bone cement system of claim 1 , wherein post-mixing the mixture is characterized as having a time-viscosity curve slope of less than or equal to about 200 Pa·s/minute for at least 5 minutes after reaching a viscosity of about 500 Pa·s.
3. The bone cement system of claim 1 , wherein the temperature of the mixture remains below about 75° C.
4. The bone cement system of claim 1 , wherein after the initial exposure period post-mixing, the mixture is characterized by a change of viscosity of less than or equal to about 30%/minute for at least three minutes after reaching about 1000 Pa·s.
5. The bone cement system of claim 1 , wherein after the initial exposure period post-mixing, the mixture is characterized by a change of viscosity of less than or equal to about 30%/minute for at least about five minutes after reaching about 4000 Pa·s.
6. The bone cement system of claim 1 , wherein after the initial exposure period post-mixing, the viscosity of the mixture increases substantially linearly until the mixture reaches the viscosity of about 2000 Pa·s.
7. The bone cement system of claim 1 , wherein the first monomer-carrying component comprises methylmethacrylate (MMA).
8. A bone cement system, comprising:
a pre-mixture comprising:
a first monomer-carrying component; and
a second polymer-carrying component, separate from the first monomer-carrying component, the second polymer-carrying component comprising a plurality of bead populations that have different mean particle sizes and an initiator in different amounts, the second polymer-carrying component comprising:
a first polymer bead population having a first mean particle size and including the initiator at a first weight percent of the first polymer bead population, wherein the initiator is integrated throughout the volume of the first polymer bead population;
a second polymer bead population having a second mean particle size smaller than the first mean particle size and including the initiator at a second weight percent of the second polymer bead population, wherein the initiator is integrated throughout the volume of the second polymer bead population; and
a third polymer bead population having a third mean particle size smaller than the second mean particle size and including the initiator at a third weight percent of the third polymer bead population, wherein the initiator is integrated throughout the volume of the third polymer bead population;
wherein upon forming a mixture of the first monomer-carrying component and the second polymer-carrying component, and after an initial exposure period post-mixing, the mixture is characterized as having a time-viscosity curve slope that remains less than or equal to about 200 Pa·s/minute at about 25 minutes.
9. The bone cement system of claim 8 , wherein after the initial exposure period post-mixing, the time-viscosity curve slope remains less than about 200 Pa·s/minute for at least about 5 minutes after reaching a viscosity of about 500 Pa·s.
10. The bone cement system of claim 8 , wherein after the initial exposure period post-mixing, the mixture has a viscosity less than about 200 Pa·s at about 15 minutes post-mixing.
11. The bone cement system of claim 8 , wherein after the initial exposure period post-mixing, the time-viscosity curve slope remains less than about 200 Pa·s/minute for at least about 25 minutes.
12. The bone cement system of claim 8 , wherein after the initial exposure period post-mixing, the time-viscosity curve slope remains less than about 100 Pa·s/minute for at least about 20 minutes.
13. The bone cement system of claim 8 , wherein after the initial exposure period post-mixing, the time-viscosity curve has a rate of change of less than about 40% over an interval of at least about 20 minutes.
14. The bone cement system of claim 8 , wherein the mixture is characterized by a post-mixing interval in which viscosity is between about 500 Pa·s and about 5000 Pa·s, and in which the change of viscosity of less than about 30%/minute within the interval.
15. The bone cement system of claim 8 , wherein after the initial exposure period post-mixing, the mixture is characterized by a change of viscosity of less than or equal to about 30%/minute for at least about three minutes after reaching about 1500 Pa·s.
16. The bone cement system of claim 8 , wherein the temperature of the mixture remains below about 75° C.
17. A bone cement system, comprising:
a pre-mixture comprising:
a first monomer-carrying component; and
a second polymer-carrying component, separate from the first monomer-carrying component, the second polymer-carrying component comprising a plurality of bead populations that have different mean particle sizes and an initiator in different amounts, the second polymer-carrying component comprising:
a first polymer bead population having a first mean particle size and including the initiator at a first weight percent of the first polymer bead population, wherein the initiator is integrated throughout the volume of the first polymer bead population; and
a second polymer bead population having a second mean particle size smaller than the first mean particle size and including the initiator at a second weight percent of the second polymer bead population, wherein the initiator is integrated throughout the volume of the second polymer bead population;
wherein upon forming a mixture of the first monomer-carrying component and the second polymer-carrying component, and after an initial exposure period post-mixing, the mixture is characterized as having a time-viscosity curve slope that remains less than or equal to about 200 Pa·s/minute until the mixture reaches a viscosity of about 2500 Pa·s, and
wherein after the initial exposure period post-mixing, the mixture is characterized by a change of viscosity of less than or equal to about 30%/minute for at least three minutes after reaching about 1000 Pa·s.
18. The bone cement system of claim 17 , wherein the time-viscosity curve slope is less than or equal to about 100 Pa·s/minute before the mixture reaches a viscosity of about 1500 Pa·s.
19. The bone cement system of claim 17 , wherein the time-viscosity curve slope is less than or equal to about 200 Pa·s/minute immediately before the mixture reaches a viscosity of about 1000 Pa·s.