Castable refractory composition
A castable refractory composition may include from 5% to 95% by weight of alumina, aluminosilicate, or mixtures thereof; from 0.5% to 1.5% by weight alkaline earth metal oxide and/or hydroxide, and 0.1% to 5% by weight of silica having a surface area of at least about 10 m 2 /g. The refractory composition may include no more than 0.5% by weight of cementitious binder. The refractory composition may release less than 25 cm 3 of hydrogen gas per kilogram of castable refractory composition upon addition of water. The refractory compositions may set on addition of water.
1. A castable refractory composition comprising:
5% to 95% by weight of alumina, aluminosilicate, or mixtures thereof;
from 0.5% to 1.5% by weight alkaline earth metal oxide and/or hydroxide; and
0.1% to 5% by weight of silica having a surface area of at least about 10 m 2 /g;
wherein the refractory composition includes no more than 0.5% by weight of cementitious binder;
wherein the refractory composition releases less than 25 cm 3 of hydrogen gas per kilogram of castable refractory composition upon addition of water; and
wherein the refractory composition sets on addition of water.
2. A castable refractory composition according to claim 1 , further comprising 0.01% to 3% by weight solid powdered organic additives.
3. A castable refractory composition according to claim 1 , further comprising 0.01% to 3% by weight soluble mineral additives.
4. A castable refractory composition according to claim 1 , further comprising up to about 1% by weight of metallic additives.
5. A castable refractory composition according to claim 1 , further comprising up to about 5% by weight of an additive or combination of additives which suppress or prevent the oxidation of carbon.
6. A castable refractory composition according to claim 1 , further comprising up to 0.5% by weight of organic fibers.
7. A castable refractory composition according to claim 1 , wherein the alumina, aluminosilicate or mixture thereof comprises a material selected from the group consisting of brown fused alumina, sintered alumina, white fused alumina, calcined alumina, reactive or semi-reactive alumina, bauxite, fused or sintered mullite, andalusite and calcined chamotte with alumina content of 30 to 75% by weight.
8. A castable refractory composition according to claim 1 , further comprising up to 70% by weight silicon carbide.
9. A castable refractory composition according to claim 8 , wherein the silicon carbide comprises particles up to about 30 mm in size.
10. A castable refractory composition according to claim 1 , further comprising up to 10% by weight carbon.
11. A castable refractory composition according to claim 10 , wherein the carbon comprises a material selected from carbon black, graphite, coke, solid hydrocarbon having a carbon residue of at least about 5% by weight after coking, and combinations thereof.
12. A castable refractory composition according to claim 1 , wherein the silica is selected from the group consisting of fumed silica, silica fume, microsilica, micro grinded silica and precipitated silica.
13. A castable refractory composition according to claim 1 , wherein the alkaline earth metal oxide comprises magnesia.
14. A castable refractory composition according to claim 13 , wherein the magnesia comprises partially hydrated magnesium oxide.
15. A castable refractory composition according to claim 1 , wherein the composition comprises less than about 0.5% by weight calcium aluminate cement and/or calcium silicate cement.
16. A castable refractory composition according to claim 1 , wherein the refractory composition is substantially free of zirconia.
17. A castable refractory composition according to claim 1 , wherein the composition is substantially free of spinel prior to casting the refractory.
18. A castable refractory composition according to claim 1 , wherein the composition is substantially free of metallic additives.
19. A castable refractory composition according to claim 1 , wherein the composition is substantially free of organic fibres.