Infiltrated Segregated Ferrous Materials
Layer-by-layer construction of metallic alloys preferably via binder jetting followed by sintering and binder removal to form a porous metallic skeleton which then may be infiltrated with an infiltrant to provide a free-standing metallic part. The part indicates a volume loss of less than or equal to 200 mm 3 as measured by ASTM G65-10 Procedure A (2010) and an un-notched impact toughness of greater than or equal to 55 J according to ASTM E21-12 (2012).
1 . A method for layer-by-layer formation of a free-standing metallic part comprising:
(a) supplying metal alloy particles comprising at least 50 weight % Fe and at least 0.5 weight % B and one or more elements selected from Cr, Ni, Si and Mn, wherein said particles have an initial level of boride phases;
(b) mixing said metallic alloy particles with a binder wherein said binder bonds said particles and forms a layer of said free-standing metallic part wherein said layer has a porosity in the range of 20% to 60%;
(c) heating said metallic alloy particles and said binder and forming a bond between said particles;
(d) sintering said metallic alloy particles and said binder by heating at a temperature of greater than or equal to 800° C. and removing said binder and forming a porous metallic skeleton;
(e) infiltrating said porous metallic skeleton with an infiltrant at a temperature of greater than or equal to 800° C. and cooling and forming said free-standing metallic part, wherein during said step of sintering and/or infiltrating, increasing the level of boride phases;
wherein said free-standing metallic part indicates a volume loss of less than or equal to 200 mm 3 as measured according to ASTM G65-10 Procedure A (2010) and an un-notched impact toughness of greater than or equal to 55 J according to ASTM E23-12 (2012).
2 . The method of claim 1 wherein said one or more elements selected from Cr, Ni, Si and Mn comprises Cr, Ni and Si.
3 . The method of claim 1 wherein said one or more elements selected from Cr, Ni, Si and Mn comprise Cr, Ni, B, Si and Mn.
4 . The method of claim 1 wherein said alloy comprises Cr at 15.0-22.0 wt. %, Ni at 5.0-15.0 wt. %, Mn at 0-3.5 wt. %, Si at 2.0-5.0 wt. %, C at 0-1.5 wt. %, B at 0.5-3.0 wt. % and Fe at 77.5-50.0 wt. %.
5 . The method of claim 1 wherein said alloy comprises Cr at 15.0-20.0 wt. %, Ni at 11.0-15.0 wt. %, Si at 2.0-5.0 wt. %, C at 0-1.5 wt. %, B at 0.5-3.0 wt. % and Fe at 71.5-55.5 wt. %.
6 . The method of claim 1 wherein said alloy comprises Cr at 17.0-22.0 wt. %, Ni at 5.0-10.0 wt. %, Mn at 0.3-3.0 wt. %, Si at 2.0-5.0 wt. %, C at 0-1.5 wt. %, B at 0.5-3.0 wt. % and Fe at 55.5-75.2 wt. %.
7 . The method of claim 1 wherein said alloy comprises Cr at 15.0-22.0 wt. %, Ni at 5.0-15.0 wt. %, Mn at 0-3.5 wt. %, Si at 2.0-5.0 wt. %, C at 0-1.5 wt. %, B at 0.5-3.0 wt. %, and Fe at 77.5-50.0 wt. %.
8 . The method of claim 1 wherein said alloy comprises Cr at 15.0-20.0 wt. %, Ni at 11.0-15.0 wt. %, Si at 0.5-2.0 wt. %; C at 0-1.5 wt. %, B at 0.5-3.0 wt. 5 and Fe at 60.0-73.0 wt. %.
9 . The method of claim 1 wherein said metal particles have a particle size distribution in the range of 0.005-0.300 mm.
10 . The method of claim 1 wherein said layer has a thickness in the range of 0.005 to 0.300 mm.
11 . The method of claim 1 wherein steps (b) through (d) are repeated to provide a layer-by-layer build up with an overall thickness in the range of 0.010 mm to 300 mm.
12 . The method of claim 1 wherein said sintering provides a metallic skeleton having a porosity of 15% to 59.1%.
13 . The method of claim 1 wherein said infiltrating of said porous metallic skeleton is configured to provide a final volume ratio of infiltrant to skeleton in the range of 15/85 to 60/40.
14 . The method of claim 1 wherein said free-standing metallic part indicates a volume loss in the range of 75 mm 3 to 200 mm 3 .
15 . The method of claim 1 wherein said free-standing metallic part indicates an an un-notched impact toughness in the range of 55 J to 100 J.
16 . A method for layer-by-layer formation of a free-standing metallic part comprising:
(a) supplying metal alloy particles comprising at least 50 weight % Fe and at least 0.5 weight % B and one or more elements selected from Cr, Ni, Si and Mn, wherein said particles have an initial level of boride phases;
(b) mixing said metallic alloy particles with a binder wherein said binder bonds said particles and forms a layer of said free-standing metallic part wherein said layer has a porosity in the range of 20% to 60%;
(c) heating said metallic alloy particles and said binder and forming a bond between said particles;
(d) sintering said metallic alloy particles and said binder by heating at a temperature of greater than or equal to 800° C. and removing said binder and forming a porous metallic skeleton having a porosity of 0% to 55%, wherein during said step of sintering, increasing the level of boride phases.
17 . The method of claim 16 wherein said alloy comprises Cr at 15.0-22.0 wt. %, Ni at 5.0-15.0 wt. %, Mn at 0-3.5 wt. %, Si at 2.0-5.0 wt. %, C at 0-1.5 wt. %, B at 0.5-3.0 wt. % and Fe at 77.5-50.0 wt. %.
18 . The method of claim 16 wherein said alloy comprises Cr at 15.0-20.0 wt. %, Ni at 11.0-15.0 wt. %, Si at 2.0-5.0 wt. %, C at 0-1.5 wt. %, B at 0.5-3.0 wt. % and Fe at 71.5-55.5 wt. %.
19 . The method of claim 16 wherein said alloy comprises Cr at 17.0-22.0 wt. %, Ni at 5.0-10.0 wt. %, Mn at 0.3-3.0 wt. %, Si at 2.0-5.0 wt. %, C at 0-1.5 wt. %, B at 0.5-3.0 wt. % and Fe at 55.5-75.2 wt. %.
20 . The method of claim 16 wherein said alloy comprises Cr at 15.0-22.0 wt. %, Ni at 5.0-15.0 wt. %, Mn at 0-3.5 wt. %, Si at 2.0-5.0 wt. %, C at 0-1.5 wt. %, B at 0.5-3.0 wt. %, and Fe at 77.5-50.0 wt. %.
21 . The method of claim 16 wherein said alloy comprises Cr at 15.0-20.0 wt. %, Ni at 11.0-15.0 wt. %, Si at 0.5-2.0 wt. %; C at 0-1.5 wt. %, B at 0.5-3.0 wt. 5 and Fe at 60.0-73.0 wt. %.